Fluocerite-(La) Mansmann M Zeitschrift fur Kristallographie 122 (1965) 375-398 Die kristallstruktur von lanthantrifluorid Locality: synthetic _database_code_amcsd 0010627 CELL PARAMETERS: 7.1900 7.1900 7.3670 90.000 90.000 120.000 SPACE GROUP: P-3c1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 329.822 Density (g/cm3): 5.917 MAX. ABS. INTENSITY / VOLUME**2: 164.1254625 RIR: 9.032 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 24.16 38.33 3.6835 0 0 2 2 24.77 26.82 3.5950 1 1 0 6 27.61 100.00 3.2308 1 1 1 12 34.87 9.63 2.5728 1 1 2 12 37.84 1.82 2.3778 0 2 2 6 40.23 1.82 2.2419 1 2 1 12 43.61 43.66 2.0756 3 0 0 6 44.69 53.84 2.0277 1 1 3 12 49.49 4.77 1.8418 0 0 4 2 50.47 16.65 1.8083 3 0 2 6 50.47 15.89 1.8083 0 3 2 6 50.79 3.19 1.7975 2 2 0 6 52.39 18.33 1.7463 2 2 1 12 56.11 4.07 1.6392 1 1 4 12 57.01 2.77 1.6154 2 2 2 12 64.21 14.05 1.4504 2 2 3 12 68.06 5.61 1.3776 3 0 4 6 68.06 5.86 1.3776 0 3 4 6 68.87 7.24 1.3633 1 1 5 12 69.13 1.93 1.3588 4 1 0 12 70.47 8.04 1.3362 1 4 1 12 70.47 7.19 1.3362 4 1 1 12 73.64 1.91 1.2864 2 2 4 12 74.42 1.43 1.2748 1 4 2 12 74.42 1.62 1.2748 4 1 2 12 77.79 1.97 1.2278 0 0 6 2 80.08 1.65 1.1983 3 3 0 6 80.85 6.42 1.1889 1 4 3 12 80.85 6.44 1.1889 4 1 3 12 83.13 2.67 1.1619 1 1 6 12 85.14 2.46 1.1395 3 3 2 12 85.15 4.47 1.1395 2 2 5 12 89.67 1.24 1.0934 4 1 4 12 89.67 1.37 1.0934 1 4 4 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.