Eulytine Segal D J, Santoro R P, Newnham R E Zeitschrift fur Kristallographie 123 (1966) 73-76 Neutron-diffraction study of Bi4Si3O12 Locality: synthetic _database_code_amcsd 0010629 CELL PARAMETERS: 10.3000 10.3000 10.3000 90.000 90.000 90.000 SPACE GROUP: I-43d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1092.727 Density (g/cm3): 6.759 MAX. ABS. INTENSITY / VOLUME**2: 228.7461721 RIR: 11.019 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.13 100.00 4.2050 2 1 1 12 24.44 4.35 3.6416 2 2 0 12 27.38 88.81 3.2571 3 1 0 24 32.53 91.67 2.7528 3 2 1 24 34.84 14.46 2.5750 4 0 0 6 43.02 45.97 2.1025 4 2 2 12 44.87 19.19 2.0200 5 1 0 24 44.87 24.25 2.0200 4 3 1 24 48.40 1.35 1.8805 5 2 1 24 50.10 1.63 1.8208 4 4 0 12 51.75 16.10 1.7664 5 3 0 24 54.95 21.06 1.6709 5 3 2 24 54.95 10.23 1.6709 6 1 1 12 56.51 10.37 1.6286 6 2 0 24 58.03 16.40 1.5893 5 4 1 24 61.01 13.08 1.5187 6 3 1 24 62.47 3.84 1.4867 4 4 4 4 63.91 11.30 1.4566 5 4 3 24 63.91 5.36 1.4566 7 1 0 24 66.74 5.02 1.4017 5 5 2 12 68.13 3.94 1.3764 6 4 2 24 69.50 1.66 1.3525 7 3 0 24 72.22 4.16 1.3081 7 3 2 24 74.90 7.36 1.2678 7 4 1 24 77.54 4.28 1.2311 6 5 3 24 78.85 6.04 1.2139 6 6 0 12 78.85 6.71 1.2139 8 2 2 12 80.16 5.80 1.1974 7 4 3 24 80.16 3.83 1.1974 8 3 1 24 82.76 5.08 1.1662 7 5 2 24 85.34 2.09 1.1374 9 1 0 24 87.91 1.79 1.1107 6 5 5 12 87.91 4.25 1.1107 9 2 1 24 89.20 2.54 1.0980 6 6 4 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.