Li2(Si.25Ge.75)2O5 Vollenkle H, Wittmann A, Nowatny H Zeitschrift fur Kristallographie 126 (1968) 37-45 Die kristallstruktur von Li2(Si0.25Ge0.75)2O5 _database_code_amcsd 0010655 CELL PARAMETERS: 5.9900 15.0500 4.9400 90.000 90.000 90.000 SPACE GROUP: Abm2 X-RAY WAVELENGTH: 1.541838 Cell Volume: 445.339 Density (g/cm3): 3.234 MAX. ABS. INTENSITY / VOLUME**2: 39.04444846 RIR: 3.931 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.76 5.26 7.5250 0 2 0 2 14.79 46.63 5.9900 1 0 0 2 18.94 13.51 4.6865 1 2 0 4 23.65 44.64 3.7625 0 4 0 2 24.09 100.00 3.6945 1 1 1 4 28.00 25.65 3.1861 1 4 0 4 29.43 11.48 3.0347 1 3 1 4 29.83 7.93 2.9950 2 0 0 2 35.56 20.41 2.5248 2 1 1 4 35.80 1.96 2.5083 0 6 0 2 36.37 20.97 2.4700 0 0 2 1 38.10 12.70 2.3621 1 5 1 4 38.36 1.20 2.3468 0 2 2 2 38.93 6.90 2.3137 1 6 0 4 39.46 3.71 2.2835 1 0 2 2 39.51 1.63 2.2810 2 3 1 4 41.32 1.60 2.1851 1 2 2 4 43.85 8.31 2.0648 0 4 2 2 45.42 4.17 1.9967 3 0 0 2 46.52 4.70 1.9521 1 4 2 4 46.56 22.13 1.9506 2 5 1 4 47.09 2.83 1.9299 3 2 0 4 47.73 3.66 1.9056 2 0 2 2 48.38 1.82 1.8813 0 8 0 2 50.87 3.81 1.7948 1 8 0 4 51.84 7.45 1.7637 3 4 0 4 51.96 2.36 1.7600 0 6 2 2 53.94 1.59 1.7000 2 4 2 4 54.33 2.82 1.6886 1 6 2 4 58.45 8.61 1.5790 1 1 3 4 59.14 4.57 1.5622 3 6 0 4 59.53 4.26 1.5528 3 0 2 2 60.46 5.78 1.5313 1 9 1 4 60.92 1.41 1.5207 3 2 2 4 61.23 2.58 1.5138 1 3 3 4 61.63 4.53 1.5050 0 10 0 2 61.97 2.40 1.4975 4 0 0 2 63.76 1.30 1.4596 1 10 0 4 64.14 1.34 1.4520 1 8 2 4 64.92 6.04 1.4364 2 1 3 4 64.97 5.59 1.4353 3 4 2 4 65.42 2.57 1.4266 4 1 1 4 66.59 5.41 1.4044 1 5 3 4 66.81 6.35 1.4002 2 9 1 4 67.29 3.14 1.3913 4 4 0 4 67.55 1.18 1.3867 2 3 3 4 68.53 2.77 1.3692 3 8 0 4 71.45 3.60 1.3203 3 6 2 4 72.67 8.68 1.3012 2 5 3 4 73.14 3.96 1.2939 4 5 1 4 73.55 2.70 1.2877 1 11 1 4 73.72 3.14 1.2852 0 10 2 2 74.03 1.29 1.2805 4 0 2 2 75.68 1.32 1.2566 1 10 2 4 78.98 2.15 1.2123 4 4 2 4 79.80 1.59 1.2018 3 10 0 4 80.14 1.96 1.1975 3 8 2 4 82.14 1.42 1.1734 0 4 4 2 83.23 2.25 1.1608 5 1 1 4 84.06 2.99 1.1514 1 9 3 4 85.65 1.17 1.1341 5 3 1 4 89.77 3.91 1.0925 2 9 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.