Pt12Si5 Gold W, Schubert K Zeitschrift fur Kristallographie 128 (1969) 406-413 Kristallstruktur von Pt12Si5 _database_code_amcsd 0010676 CELL PARAMETERS: 13.4040 13.4040 5.4510 90.000 90.000 90.000 SPACE GROUP: P4/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 979.366 Density (g/cm3): 16.826 MAX. ABS. INTENSITY / VOLUME**2: 1626.997611 RIR: 31.484 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.33 100.00 9.4781 1 1 0 4 20.96 1.87 4.2387 1 3 0 4 26.64 1.73 3.3461 3 1 1 8 26.64 6.90 3.3461 1 3 1 8 29.07 1.19 3.0713 2 3 1 8 29.81 12.58 2.9972 4 2 0 4 34.11 2.47 2.6287 5 1 0 4 34.23 5.70 2.6194 1 1 2 8 35.56 10.11 2.5247 2 0 2 8 37.97 11.41 2.3695 4 4 0 4 38.09 4.44 2.3626 2 2 2 8 38.70 1.12 2.3268 3 0 2 8 39.19 2.91 2.2988 5 3 0 4 39.30 1.37 2.2925 1 3 2 8 40.37 11.20 2.2340 6 0 0 4 41.06 1.35 2.1981 3 2 2 8 41.06 1.83 2.1981 2 3 2 8 42.66 6.00 2.1194 6 2 0 4 42.66 10.39 2.1194 2 6 0 4 43.32 1.15 2.0886 4 1 2 8 44.95 15.67 2.0165 4 2 2 8 47.99 1.22 1.8956 7 1 0 4 48.09 1.19 1.8921 5 1 2 8 49.01 2.53 1.8588 6 4 0 4 51.08 1.38 1.7882 4 4 2 8 51.95 1.56 1.7600 7 3 0 4 52.04 1.46 1.7572 5 3 2 8 52.63 1.81 1.7389 1 2 3 8 54.88 2.32 1.6731 2 6 2 8 54.98 1.16 1.6700 3 1 3 8 54.98 2.77 1.6700 1 3 3 8 58.16 1.17 1.5861 1 4 3 8 62.85 1.52 1.4785 7 3 2 8 63.38 2.63 1.4676 2 5 3 8 67.04 1.71 1.3960 2 8 2 8 67.04 1.12 1.3960 8 2 2 8 70.22 2.24 1.3404 8 6 0 4 70.22 1.26 1.3404 6 8 0 4 71.82 2.10 1.3144 10 2 0 4 71.90 2.57 1.3132 4 8 2 8 71.90 1.91 1.3132 8 4 2 8 71.99 1.52 1.3117 7 1 3 8 71.99 1.12 1.3117 5 5 3 8 76.55 2.14 1.2445 4 10 0 4 81.26 1.16 1.1839 10 2 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.