Kosnarite Sljukic M, Matkovic B, Prodic B, Anderson D Zeitschrift fur Kristallographie 130 (1969) 148-161 The crystal structure of KZr2(PO4)3 Locality: synthetic _database_code_amcsd 0010697 CELL PARAMETERS: 8.7100 8.7100 23.8900 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1569.579 Density (g/cm3): 3.214 MAX. ABS. INTENSITY / VOLUME**2: 28.73743787 RIR: 2.911 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.89 23.70 6.3779 0 1 2 6 18.95 41.64 4.6824 1 0 4 6 20.39 90.83 4.3550 1 1 0 6 23.28 71.49 3.8209 1 1 3 12 27.98 37.05 3.1889 0 2 4 6 30.42 100.00 2.9386 1 1 6 12 31.60 7.34 2.8309 2 1 1 12 32.24 4.66 2.7766 0 1 8 6 34.87 8.12 2.5729 2 1 4 12 35.71 33.02 2.5144 3 0 0 6 38.45 3.53 2.3412 2 0 8 6 39.57 1.70 2.2775 1 0 10 6 39.77 4.00 2.2666 1 1 9 12 41.26 1.22 2.1880 2 1 7 12 41.47 5.60 2.1775 2 2 0 6 42.52 12.96 2.1260 0 3 6 6 42.52 2.18 2.1260 3 0 6 6 43.07 1.79 2.1004 2 2 3 12 43.91 7.86 2.0621 1 2 8 12 43.94 1.50 2.0607 3 1 2 12 44.91 7.53 2.0182 0 2 10 6 45.57 2.50 1.9908 0 0 12 2 45.96 7.85 1.9744 1 3 4 12 47.60 30.77 1.9105 2 2 6 12 48.90 2.41 1.8627 0 4 2 6 49.80 20.43 1.8311 2 1 10 12 50.40 1.01 1.8106 1 1 12 12 51.22 3.81 1.7836 1 3 7 12 53.48 5.77 1.7134 3 1 8 12 54.51 1.03 1.6835 2 2 9 12 55.19 3.57 1.6644 0 1 14 6 55.27 7.20 1.6621 3 2 4 12 55.85 20.94 1.6460 4 1 0 12 56.56 1.04 1.6271 2 3 5 12 57.14 2.03 1.6120 4 1 3 12 57.83 3.18 1.5945 0 4 8 6 58.66 12.08 1.5739 1 3 10 12 59.20 3.34 1.5608 0 3 12 6 59.20 3.07 1.5608 3 0 12 6 59.45 7.61 1.5547 2 0 14 6 60.90 7.66 1.5212 1 4 6 12 60.90 7.76 1.5212 4 1 6 12 62.05 1.50 1.4958 1 1 15 12 62.77 4.28 1.4802 4 0 10 6 63.52 1.93 1.4647 1 0 16 6 63.54 6.67 1.4642 1 2 14 12 63.61 3.17 1.4627 0 5 4 6 64.15 5.54 1.4517 3 3 0 6 66.75 3.23 1.4015 3 2 10 12 67.46 1.20 1.3883 0 2 16 6 67.56 2.12 1.3866 2 4 4 12 68.84 3.92 1.3638 3 3 6 12 69.49 1.34 1.3526 5 1 1 12 71.30 2.80 1.3227 2 1 16 12 71.32 4.93 1.3223 3 1 14 12 71.39 6.35 1.3212 5 1 4 12 75.41 1.14 1.2605 1 2 17 12 75.50 1.97 1.2592 5 1 7 12 75.64 5.08 1.2572 6 0 0 6 78.07 2.07 1.2241 2 4 10 12 78.76 5.17 1.2150 2 3 14 12 79.32 1.22 1.2079 5 2 0 12 81.60 4.24 1.1798 0 1 20 6 82.18 1.01 1.1730 3 3 12 12 83.67 1.68 1.1558 5 2 6 12 84.24 1.20 1.1495 1 5 11 12 85.22 1.19 1.1388 2 0 20 6 85.99 2.01 1.1305 3 2 16 12 86.01 1.42 1.1302 5 0 14 6 88.81 1.89 1.1017 1 2 20 12 88.92 1.78 1.1006 4 3 10 12 89.61 2.10 1.0940 4 2 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.