Sr(NO3)2*4H2O Ribar B, Matkovic B, Sljukic M Zeitschrift fur Kristallographie 135 (1972) 137-144 Die Kristallstruktur von strontiumnitrat-tetrahydrat, Sr(NO3)2*4H2O _database_code_amcsd 0010727 CELL PARAMETERS: 11.1200 14.1700 6.3400 90.000 123.750 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 830.635 Density (g/cm3): 2.337 MAX. ABS. INTENSITY / VOLUME**2: 13.24770849 RIR: 1.845 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.43 5.04 7.7433 1 1 0 4 12.49 32.82 7.0850 0 2 0 2 15.31 100.00 5.7864 -1 1 1 4 19.20 6.38 4.6230 2 0 0 2 21.12 10.66 4.2063 1 3 0 4 21.23 13.61 4.1848 -2 2 1 4 22.97 45.45 3.8717 2 2 0 4 23.49 6.80 3.7875 -1 3 1 4 24.45 10.24 3.6403 1 1 1 4 24.84 6.77 3.5840 -3 1 1 4 29.66 1.07 3.0116 3 1 0 4 30.31 6.25 2.9485 -1 1 2 4 30.35 11.51 2.9450 1 3 1 4 30.40 31.65 2.9403 0 4 1 4 30.63 48.94 2.9183 -3 1 2 4 30.67 26.39 2.9149 -3 3 1 4 30.91 16.70 2.8932 -2 2 2 4 31.82 7.98 2.8119 2 4 0 4 33.06 3.32 2.7096 1 5 0 4 34.01 3.66 2.6358 0 0 2 2 34.54 30.24 2.5968 2 2 1 4 34.59 8.02 2.5930 -4 0 2 2 34.67 18.02 2.5872 -1 5 1 4 34.76 3.15 2.5811 3 3 0 4 35.60 17.73 2.5217 -3 3 2 4 36.37 9.37 2.4704 0 2 2 4 36.91 3.59 2.4351 -4 2 2 4 38.10 5.49 2.3621 -2 4 2 4 38.10 1.54 2.3617 0 6 0 2 39.80 3.09 2.2646 1 5 1 4 40.06 3.57 2.2509 -3 5 1 4 41.07 11.23 2.1975 4 2 0 4 41.18 26.01 2.1923 2 4 1 4 41.85 7.74 2.1585 3 1 1 4 41.92 2.61 2.1553 0 6 1 4 42.04 23.80 2.1493 -2 6 1 4 42.34 24.08 2.1348 -5 1 1 4 42.76 6.26 2.1146 0 4 2 4 43.24 1.86 2.0924 -4 4 2 4 43.29 9.27 2.0899 -3 1 3 4 43.38 7.62 2.0861 3 5 0 4 43.85 6.30 2.0648 -1 5 2 4 44.08 9.77 2.0544 -3 5 2 4 44.97 2.08 2.0160 1 3 2 4 45.65 5.31 1.9872 -5 3 2 4 45.77 3.76 1.9823 3 3 1 4 45.89 4.62 1.9774 1 7 0 4 46.05 2.82 1.9711 -4 2 3 4 46.22 3.47 1.9639 -5 3 1 4 46.94 2.43 1.9358 4 4 0 4 47.12 7.36 1.9288 -3 3 3 4 47.43 16.62 1.9169 -1 1 3 4 48.04 2.26 1.8938 -2 6 2 4 48.09 6.69 1.8921 -5 1 3 4 48.33 3.84 1.8834 2 0 2 2 49.19 5.74 1.8522 -6 0 2 2 50.12 3.08 1.8202 2 2 2 4 50.95 5.12 1.7924 -4 6 1 4 50.96 3.02 1.7920 -6 2 2 4 51.01 2.44 1.7903 -1 3 3 4 51.15 1.26 1.7858 -2 4 3 4 51.46 2.21 1.7757 -4 4 3 4 51.60 1.43 1.7713 0 8 0 2 52.21 1.54 1.7521 1 5 2 4 52.40 1.26 1.7460 -4 6 2 4 52.82 3.21 1.7331 -5 5 2 4 54.21 4.15 1.6920 3 7 0 4 54.61 3.51 1.6805 -1 7 2 4 54.66 3.42 1.6790 0 8 1 4 54.76 4.07 1.6762 -2 8 1 4 54.81 2.56 1.6749 -3 7 2 4 55.24 1.98 1.6630 2 4 2 4 55.64 1.81 1.6519 4 6 0 4 56.03 1.01 1.6414 -6 4 2 4 58.27 2.93 1.5834 -5 5 3 4 58.36 2.55 1.5811 -6 4 1 4 58.65 1.06 1.5742 0 4 3 4 59.56 3.09 1.5521 1 9 0 4 59.69 2.21 1.5490 -4 6 3 4 59.71 2.87 1.5487 5 5 0 4 59.80 2.03 1.5465 -4 2 4 4 61.52 1.12 1.5072 -2 0 4 2 61.73 1.41 1.5028 -7 3 2 4 61.92 4.27 1.4986 1 7 2 4 62.08 2.56 1.4950 5 1 1 4 62.19 1.29 1.4927 1 3 3 4 62.26 3.83 1.4911 -6 0 4 2 62.34 3.03 1.4896 -4 8 1 4 62.63 2.32 1.4832 -7 1 1 4 63.06 2.23 1.4743 -2 2 4 4 63.29 1.63 1.4694 -7 3 3 4 63.79 1.58 1.4592 -6 2 4 4 64.41 2.31 1.4466 -4 4 4 4 65.11 1.36 1.4326 5 3 1 4 65.59 2.24 1.4233 4 6 1 4 65.65 1.07 1.4222 -7 3 1 4 66.13 2.37 1.4131 6 4 0 4 66.30 1.57 1.4098 0 6 3 4 66.71 1.61 1.4021 3 9 0 4 67.06 3.26 1.3956 -1 9 2 4 67.07 3.36 1.3955 4 0 2 2 67.10 2.16 1.3949 -6 6 3 4 68.17 2.38 1.3756 1 5 3 4 68.43 1.47 1.3710 -3 5 4 4 68.53 2.28 1.3692 4 2 2 4 68.58 1.11 1.3684 0 10 1 4 68.76 2.02 1.3653 5 7 0 4 69.09 1.01 1.3594 -1 3 4 4 69.22 2.39 1.3573 -7 5 3 4 69.40 1.03 1.3542 -8 2 3 4 69.58 1.64 1.3512 -8 2 2 4 69.93 1.31 1.3452 -2 8 3 4 70.19 1.33 1.3409 -4 8 3 4 73.66 2.03 1.2860 1 9 2 4 73.69 1.46 1.2856 -8 4 3 4 74.35 1.71 1.2759 1 11 0 4 74.38 1.40 1.2753 -8 2 4 4 74.61 1.76 1.2720 7 3 0 4 74.80 1.53 1.2692 -1 5 4 4 75.45 2.35 1.2599 -4 10 1 4 75.46 1.11 1.2598 3 7 2 4 76.09 1.82 1.2509 -6 8 1 4 76.29 1.03 1.2481 0 10 2 4 76.30 1.56 1.2480 -7 7 2 4 76.34 1.54 1.2475 0 8 3 4 76.96 1.46 1.2389 -3 7 4 4 77.09 1.83 1.2371 -6 8 3 4 77.30 1.73 1.2344 -5 7 4 4 78.47 1.15 1.2189 1 11 1 4 79.08 1.22 1.2110 -8 4 1 4 79.31 1.52 1.2081 4 10 0 4 79.41 1.54 1.2067 2 6 3 4 80.04 1.14 1.1988 5 9 0 4 80.17 1.03 1.1972 7 5 0 4 81.95 1.37 1.1757 1 3 4 4 82.53 2.11 1.1689 -2 10 3 4 83.68 1.23 1.1557 8 0 0 2 84.09 1.29 1.1511 -7 7 4 4 85.36 1.60 1.1373 6 6 1 4 86.46 1.12 1.1255 3 9 2 4 88.03 1.52 1.1095 4 10 1 4 88.25 1.65 1.1072 -5 9 4 4 88.97 1.12 1.1002 2 8 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.