Dansite Burzlaff H, Grube H H Zeitschrift fur Kristallographie 152 (1980) 83-93 Strukturverfeinerung und zwillingsgesetz am Zn-d'ansit _database_code_amcsd 0010830 CELL PARAMETERS: 15.9132 15.9132 15.9132 90.000 90.000 90.000 SPACE GROUP: I-43d X-RAY WAVELENGTH: 1.541838 Cell Volume: 4029.699 Density (g/cm3): 2.662 MAX. ABS. INTENSITY / VOLUME**2: 9.029191876 RIR: 1.104 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.63 26.33 6.4965 2 1 1 12 15.75 1.68 5.6262 2 2 0 12 20.89 22.70 4.2530 3 2 1 24 22.35 25.05 3.9783 4 0 0 6 25.03 9.72 3.5583 4 2 0 24 26.27 93.37 3.3927 3 3 2 12 28.60 5.18 3.1208 5 1 0 24 28.60 43.90 3.1208 4 3 1 24 30.77 16.05 2.9053 5 2 1 24 31.81 100.00 2.8131 4 4 0 12 32.82 6.50 2.7291 5 3 0 24 34.75 21.71 2.5815 6 1 1 12 34.75 22.40 2.5815 5 3 2 24 35.68 30.79 2.5161 6 2 0 24 36.60 14.32 2.4555 5 4 1 24 38.36 3.59 2.3463 6 3 1 24 39.22 8.97 2.2969 4 4 4 4 40.07 2.65 2.2505 7 1 0 24 40.07 7.27 2.2505 5 4 3 24 41.71 2.69 2.1655 7 2 1 24 41.71 2.94 2.1655 6 3 3 12 41.71 12.52 2.1655 5 5 2 12 44.85 10.17 2.0210 7 3 2 24 44.85 8.63 2.0210 6 5 1 24 45.61 4.59 1.9892 8 0 0 6 47.09 1.35 1.9298 8 2 0 24 47.82 18.49 1.9020 6 5 3 24 49.26 7.94 1.8499 7 4 3 24 49.26 2.14 1.8499 7 5 0 24 50.66 1.56 1.8018 7 5 2 24 52.04 4.54 1.7573 9 1 0 24 53.39 5.43 1.7160 7 6 1 24 53.39 12.12 1.7160 9 2 1 24 53.39 13.49 1.7160 6 5 5 12 54.06 6.03 1.6964 6 6 4 12 54.72 1.67 1.6774 9 3 0 24 54.72 1.79 1.6774 8 5 1 24 56.03 4.02 1.6413 7 6 3 24 56.03 2.19 1.6413 9 3 2 24 56.68 6.37 1.6241 8 4 4 12 57.32 3.87 1.6075 8 5 3 24 58.59 1.31 1.5756 7 7 2 12 59.21 3.66 1.5604 10 2 0 24 59.21 2.75 1.5604 8 6 2 24 61.07 3.43 1.5173 7 6 5 24 61.07 3.11 1.5173 9 5 2 24 62.30 3.71 1.4904 8 7 1 24 63.50 4.50 1.4649 9 6 1 24 64.10 3.50 1.4527 10 4 2 24 64.70 1.60 1.4407 9 5 4 24 65.88 1.49 1.4177 11 2 1 24 65.88 3.10 1.4177 10 5 1 24 65.88 1.02 1.4177 9 6 3 24 66.47 4.14 1.4065 8 8 0 12 67.06 2.04 1.3957 9 7 0 24 68.22 2.46 1.3747 10 5 3 24 68.80 1.91 1.3645 8 6 6 12 69.38 2.19 1.3546 11 4 1 24 72.22 1.71 1.3081 12 2 0 24 72.79 1.75 1.2993 10 5 5 12 72.79 3.81 1.2993 11 5 2 24 73.91 2.16 1.2823 12 3 1 24 77.24 2.04 1.2351 11 6 3 24 77.24 3.05 1.2351 9 7 6 24 77.79 1.02 1.2277 10 8 2 24 81.08 1.03 1.1861 12 6 0 24 84.87 1.47 1.1425 11 8 3 24 85.95 1.32 1.1309 13 5 2 24 85.95 1.81 1.1309 10 7 7 12 86.49 1.23 1.1252 14 2 0 24 86.49 1.05 1.1252 10 8 6 24 88.11 2.97 1.1087 11 7 6 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.