Sb2MoO6 Laarif A, Theobald F R, Vivier H, Hewat A W Zeitschrift fur Kristallographie 167 (1984) 117-124 Crystal structure of Sb2MoO6 Note: X-ray single crystal refinement Note: synthetic polymorph of biehlite _database_code_amcsd 0010869 CELL PARAMETERS: 7.4810 7.5040 10.1200 70.430 70.910 83.350 SPACE GROUP: P-1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 505.842 Density (g/cm3): 5.717 MAX. ABS. INTENSITY / VOLUME**2: 57.96563700 RIR: 3.301 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.29 15.85 4.3776 -1 1 1 2 20.39 16.95 4.3557 1 -1 1 2 23.95 3.17 3.7157 0 2 1 2 24.04 2.19 3.7017 2 0 1 2 25.19 1.78 3.5352 0 2 0 2 25.19 1.65 3.5347 2 0 0 2 25.55 1.10 3.4864 1 2 1 2 26.50 10.26 3.3639 -1 1 2 2 26.61 94.82 3.3493 0 2 2 2 26.65 1.19 3.3449 1 2 2 2 26.66 7.60 3.3440 1 -1 2 2 26.78 100.00 3.3293 2 0 2 2 28.14 2.81 3.1708 1 2 0 2 28.30 1.22 3.1530 -1 2 0 2 28.31 1.68 3.1528 -2 1 0 2 28.59 1.67 3.1219 -1 2 1 2 29.54 67.14 3.0239 0 0 3 2 29.82 59.71 2.9961 -2 0 1 2 29.89 60.23 2.9893 0 -2 1 2 31.08 1.23 2.8773 1 2 3 2 31.25 1.52 2.8619 -2 1 1 2 32.23 1.55 2.7774 2 2 2 2 32.55 46.05 2.7510 2 2 1 2 33.62 1.46 2.6659 -2 -1 1 2 34.92 4.12 2.5697 2 2 3 2 35.80 7.04 2.5084 2 2 0 2 36.06 19.51 2.4908 -2 2 0 2 36.73 1.07 2.4466 -2 0 2 2 37.00 2.44 2.4298 1 3 2 2 37.01 1.57 2.4292 1 -2 2 2 37.12 1.20 2.4219 3 1 2 2 37.80 1.16 2.3802 1 2 4 2 38.13 1.56 2.3600 -1 2 3 2 39.60 4.38 2.2760 -1 3 1 2 39.71 3.13 2.2696 3 -1 1 2 39.86 3.41 2.2618 0 2 4 2 40.08 18.98 2.2499 2 2 4 2 40.08 2.57 2.2496 2 0 4 2 40.25 2.31 2.2405 1 3 0 2 40.26 3.37 2.2403 3 1 0 2 40.43 1.68 2.2311 -1 3 0 2 40.43 2.42 2.2309 -3 1 0 2 40.99 1.07 2.2020 -2 -1 2 2 45.35 1.13 1.9997 -3 -1 1 2 45.37 5.37 1.9990 -1 3 3 2 45.40 1.74 1.9977 -1 -3 1 2 45.67 5.93 1.9863 3 -1 3 2 47.13 12.58 1.9282 -2 2 3 2 47.43 14.44 1.9170 2 -2 3 2 48.61 14.58 1.8728 0 2 5 2 48.64 16.16 1.8718 -2 -2 2 2 48.83 1.53 1.8652 -3 1 2 2 48.86 16.23 1.8642 2 0 5 2 49.00 1.41 1.8589 1 4 2 2 49.01 1.95 1.8586 1 -3 2 2 49.30 11.02 1.8482 0 4 1 2 49.41 12.53 1.8447 4 0 1 2 50.21 1.06 1.8170 4 1 1 2 50.57 1.52 1.8051 1 3 5 2 50.80 1.02 1.7972 3 1 5 2 50.92 1.06 1.7932 0 4 3 2 51.30 3.53 1.7809 -1 3 4 2 51.67 2.26 1.7690 3 -1 4 2 52.49 2.04 1.7432 2 4 2 2 52.59 1.67 1.7402 4 2 2 2 52.67 10.38 1.7377 2 4 3 2 52.81 11.45 1.7334 4 2 3 2 53.53 1.31 1.7120 -1 4 0 2 53.66 1.08 1.7081 -1 1 5 2 54.38 11.95 1.6872 -2 0 4 2 54.55 13.12 1.6822 0 -2 4 2 54.82 6.84 1.6746 0 4 4 2 55.18 9.02 1.6646 4 0 4 2 55.33 1.68 1.6605 2 2 6 2 55.69 2.68 1.6504 -3 1 3 2 55.95 1.93 1.6434 1 -3 3 2 56.26 2.64 1.6352 -3 3 1 2 56.39 3.99 1.6317 3 -3 1 2 58.19 5.40 1.5854 2 4 0 2 58.20 5.57 1.5853 4 2 0 2 58.38 1.05 1.5808 -1 -4 1 2 59.02 1.68 1.5652 2 4 5 2 59.13 2.45 1.5624 -3 3 2 2 59.19 2.75 1.5609 -2 4 2 2 59.23 1.30 1.5600 4 2 5 2 59.38 1.26 1.5564 3 -3 2 2 59.45 3.55 1.5548 4 -2 2 2 60.99 3.76 1.5193 -4 2 1 2 61.10 3.88 1.5166 2 -4 1 2 61.31 6.92 1.5120 0 0 6 2 61.94 4.11 1.4981 -4 0 2 2 62.10 4.36 1.4947 0 -4 2 2 63.68 1.16 1.4614 -4 -2 1 2 63.71 1.20 1.4607 -2 -4 1 2 63.96 1.95 1.4557 1 5 1 2 64.04 1.26 1.4539 5 1 1 2 64.36 1.99 1.4474 1 5 4 2 64.69 1.33 1.4409 5 1 4 2 64.69 7.99 1.4408 2 2 7 2 64.81 3.08 1.4386 2 4 6 2 65.05 3.85 1.4339 4 2 6 2 65.37 1.92 1.4276 -1 5 2 2 65.61 2.27 1.4229 5 -1 2 2 66.91 1.49 1.3984 4 4 3 2 66.93 1.29 1.3980 -1 5 3 2 67.44 1.50 1.3887 4 4 4 2 68.17 2.57 1.3755 4 4 2 2 69.74 2.93 1.3484 4 4 5 2 70.02 1.10 1.3436 -3 3 4 2 70.48 1.64 1.3360 3 -3 4 2 71.33 2.01 1.3223 -5 1 1 2 71.43 1.61 1.3206 1 -5 1 2 73.01 2.80 1.2959 -2 2 6 2 73.46 3.66 1.2891 2 -2 6 2 73.67 1.06 1.2859 -2 4 5 2 74.24 1.90 1.2775 4 -2 5 2 76.10 1.07 1.2508 0 4 7 2 76.62 1.89 1.2436 4 0 7 2 77.38 2.90 1.2333 -2 -2 5 2 77.73 1.32 1.2286 -3 3 5 2 78.67 1.24 1.2162 -3 5 1 2 79.07 2.01 1.2111 -4 -2 3 2 79.17 2.03 1.2098 -2 -4 3 2 79.25 1.48 1.2088 -3 5 0 2 79.26 2.40 1.2087 -5 3 0 2 79.35 1.50 1.2075 4 4 7 2 79.70 1.18 1.2031 6 2 2 2 80.32 2.06 1.1954 0 2 8 2 80.61 2.52 1.1918 2 0 8 2 81.29 1.07 1.1835 6 2 5 2 82.11 2.00 1.1738 -4 -4 1 2 82.99 1.20 1.1636 5 -3 3 2 86.52 1.01 1.1249 4 4 8 2 87.86 1.74 1.1112 -2 0 7 2 88.00 1.05 1.1098 6 0 6 2 88.11 2.06 1.1087 0 -2 7 2 88.28 1.10 1.1070 -4 0 5 2 88.63 1.42 1.1035 0 -4 5 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.