UBi2 Pearson W B Zeitschrift fur Kristallographie 171 (1985) 23-39 The Cu2Sb and related structures _database_code_amcsd 0010892 CELL PARAMETERS: 4.4450 4.4450 8.9080 90.000 90.000 90.000 SPACE GROUP: P4/nmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 176.005 Density (g/cm3): 12.376 MAX. ABS. INTENSITY / VOLUME**2: 450.7317253 RIR: 11.858 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.93 2.89 8.9080 0 0 1 2 19.93 1.26 4.4540 0 0 2 2 22.35 5.58 3.9773 1 0 1 8 28.37 11.42 3.1463 1 0 2 8 28.40 21.06 3.1431 1 1 0 4 30.10 46.45 2.9693 0 0 3 2 30.15 99.67 2.9640 1 1 1 8 34.94 100.00 2.5681 1 1 2 8 36.39 32.61 2.4691 1 0 3 8 40.51 2.61 2.2270 0 0 4 2 40.59 61.35 2.2225 2 0 0 4 41.85 2.81 2.1584 1 1 3 8 46.83 1.44 1.9401 2 1 1 16 50.21 7.88 1.8171 1 1 4 8 50.26 4.23 1.8153 2 1 2 16 51.35 37.58 1.7793 2 0 3 8 55.57 12.20 1.6537 1 0 5 8 55.64 17.07 1.6519 2 1 3 16 58.69 3.12 1.5731 2 0 4 8 58.75 18.38 1.5715 2 2 0 4 59.66 10.13 1.5499 1 1 5 8 62.56 1.03 1.4847 0 0 6 2 66.38 7.84 1.4082 1 0 6 8 66.52 3.00 1.4056 3 1 0 8 67.42 14.65 1.3890 2 2 3 8 67.45 15.76 1.3885 3 1 1 16 70.10 1.46 1.3424 1 1 6 8 70.22 20.69 1.3405 3 1 2 16 71.05 10.35 1.3267 2 1 5 16 71.11 3.63 1.3258 3 0 3 8 73.80 1.41 1.2840 2 2 4 8 77.28 1.97 1.2345 2 0 6 8 80.80 8.08 1.1895 2 1 6 16 80.87 3.03 1.1887 3 1 4 16 81.62 1.06 1.1796 1 1 7 8 85.18 2.87 1.1392 3 0 5 8 85.23 4.05 1.1386 3 2 3 16 87.85 4.81 1.1113 4 0 0 4 88.55 1.13 1.1044 2 0 7 8 88.63 5.48 1.1035 3 1 5 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.