Eucryptite Hesse K F Zeitschrift fur Kristallographie 172 (1985) 147-151 Crystal structures of natural and synthetic alpha-eucryptite, LiAlSiO4 Locality: synthetic _database_code_amcsd 0010936 CELL PARAMETERS: 13.4730 13.4730 9.0010 90.000 90.000 120.000 SPACE GROUP: R-3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1414.979 Density (g/cm3): 2.661 MAX. ABS. INTENSITY / VOLUME**2: 7.848308799 RIR: 0.960 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.14 42.59 6.7365 1 1 0 6 21.16 31.23 4.1990 0 1 2 6 22.45 39.01 3.9603 2 1 1 6 22.45 56.04 3.9603 3 -1 1 6 22.87 31.06 3.8893 3 0 0 6 24.99 7.12 3.5634 2 0 2 6 26.46 100.00 3.3682 2 2 0 6 28.33 8.40 3.1499 1 2 2 6 28.33 7.79 3.1499 -1 3 2 6 29.33 2.29 3.0453 -1 4 1 6 29.33 9.26 3.0453 1 3 1 6 32.67 44.23 2.7408 1 1 3 6 32.67 44.87 2.7408 2 -1 3 6 35.25 65.17 2.5462 4 1 0 6 36.71 3.40 2.4478 0 4 2 6 37.87 15.36 2.3756 0 3 3 6 37.87 14.65 2.3756 3 0 3 6 40.16 15.08 2.2455 3 3 0 6 40.25 3.75 2.2404 2 2 3 6 40.25 3.58 2.2404 4 -2 3 6 42.19 2.66 2.1417 2 4 1 6 43.69 1.77 2.0717 5 0 2 6 46.71 6.46 1.9447 6 0 0 6 46.79 4.01 1.9413 -1 5 3 6 46.79 3.54 1.9413 4 1 3 6 48.53 5.74 1.8761 7 -3 1 6 48.53 1.55 1.8761 4 3 1 6 48.74 12.64 1.8684 2 5 0 6 50.79 17.19 1.7978 6 -3 3 6 50.79 15.30 1.7978 3 3 3 6 51.28 3.65 1.7817 4 0 4 6 55.10 1.50 1.6667 1 2 5 6 55.10 4.24 1.6667 -1 3 5 6 55.54 1.02 1.6547 6 1 2 6 56.12 1.35 1.6390 -3 8 1 6 56.38 6.93 1.6319 0 6 3 6 56.38 7.38 1.6319 6 0 3 6 56.84 2.04 1.6198 0 5 4 6 57.91 1.84 1.5925 6 2 1 6 58.69 1.16 1.5732 3 1 5 6 59.85 8.29 1.5455 1 7 0 6 59.85 7.00 1.5455 7 1 0 6 60.84 2.37 1.5226 -2 8 2 6 61.85 15.99 1.5002 0 0 6 2 63.26 1.67 1.4700 3 6 0 6 63.26 1.95 1.4700 6 3 0 6 63.75 1.96 1.4598 4 3 4 6 65.87 1.04 1.4179 4 5 2 6 68.27 17.97 1.3739 1 7 3 6 68.27 5.76 1.3739 -1 8 3 6 68.27 17.89 1.3739 8 -1 3 6 68.27 5.96 1.3739 7 1 3 6 68.47 4.05 1.3704 2 2 6 6 68.47 4.03 1.3704 4 -2 6 6 69.81 3.29 1.3473 5 5 0 6 71.46 7.90 1.3201 -3 9 3 6 71.46 7.66 1.3201 6 3 3 6 71.93 1.55 1.3127 3 4 5 6 72.97 10.05 1.2964 9 0 0 6 73.23 5.81 1.2925 4 1 6 6 73.23 5.80 1.2925 -1 5 6 6 76.55 1.38 1.2446 9 -4 4 6 77.29 2.36 1.2345 3 -1 7 6 77.69 1.75 1.2291 10 -5 3 6 77.69 1.72 1.2291 5 5 3 6 79.68 1.47 1.2034 -2 8 5 6 80.35 1.34 1.1950 1 3 7 6 80.94 1.36 1.1878 0 6 6 6 80.94 1.64 1.1878 6 0 6 6 81.56 2.08 1.1803 9 1 2 6 82.27 1.76 1.1719 2 8 3 6 82.27 1.59 1.1719 10 -2 3 6 82.45 1.68 1.1698 2 5 6 6 82.45 1.89 1.1698 7 -2 6 6 86.09 1.74 1.1295 0 10 2 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.