Hatrurite Nishi F, Takeuchi Y, Maki I Zeitschrift fur Kristallographie 172 (1985) 297-314 Tricalcium silicate Ca3O[SiO4]: The monoclinic superstructure Locality: synthetic _database_code_amcsd 0010938 CELL PARAMETERS: 33.0830 7.0270 18.4990 90.000 94.120 90.000 SPACE GROUP: Cm X-RAY WAVELENGTH: 1.541838 Cell Volume: 4289.427 Density (g/cm3): 3.181 MAX. ABS. INTENSITY / VOLUME**2: 7.599550300 RIR: 0.778 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.91 4.54 5.9410 4 0 2 1 14.96 9.56 5.9217 3 1 0 2 16.12 1.08 5.4996 6 0 0 1 16.20 2.38 5.4725 1 1 2 2 22.98 3.05 3.8705 -8 0 2 1 23.06 5.00 3.8569 -1 1 4 2 25.24 3.77 3.5288 7 1 2 2 25.35 2.13 3.5135 0 2 0 2 28.14 2.39 3.1716 -6 0 5 1 29.39 34.00 3.0385 10 0 2 1 29.54 77.91 3.0242 4 2 2 2 30.08 10.29 2.9705 8 0 4 1 30.18 20.43 2.9608 6 2 0 2 32.32 100.00 2.7702 -6 0 6 1 32.56 44.30 2.7498 12 0 0 1 32.73 85.37 2.7362 2 2 4 2 33.28 1.68 2.6925 -11 1 2 2 33.35 1.88 2.6870 3 1 6 2 33.40 2.65 2.6830 -4 2 4 2 33.63 1.08 2.6647 -8 2 1 2 34.42 41.17 2.6055 6 0 6 1 34.48 80.36 2.6015 -8 2 2 2 36.74 5.04 2.4465 -6 0 7 1 38.75 5.57 2.3240 -14 0 2 1 38.92 15.50 2.3140 0 2 6 2 38.94 1.91 2.3131 6 0 7 1 39.02 1.25 2.3085 -9 1 6 2 39.14 1.23 2.3017 11 1 4 2 39.20 1.05 2.2983 10 2 2 2 39.33 1.55 2.2910 3 3 0 2 39.51 2.03 2.2810 -10 2 3 2 41.40 4.99 2.1812 -13 1 4 2 41.40 15.00 2.1810 4 0 8 1 41.42 31.99 2.1801 -10 2 4 2 41.48 5.61 2.1768 1 1 8 2 41.51 6.03 2.1754 -6 2 6 2 41.70 5.13 2.1661 9 1 6 2 41.71 6.37 2.1654 12 2 0 2 41.72 1.40 2.1649 -12 2 1 2 41.85 6.27 2.1586 -5 3 2 2 43.32 1.02 2.0886 -1 3 4 2 43.84 2.06 2.0651 -10 2 5 2 45.77 3.91 1.9826 16 0 2 1 45.82 1.33 1.9803 12 0 6 1 45.98 3.83 1.9739 9 3 0 2 46.01 6.79 1.9728 5 3 4 2 46.95 7.34 1.9353 -16 0 4 1 47.13 17.33 1.9285 -2 2 8 2 49.72 3.42 1.8338 14 2 3 2 49.74 2.02 1.8332 18 0 0 1 50.00 5.45 1.8242 3 3 6 2 50.13 3.67 1.8197 -12 2 6 2 50.14 1.95 1.8193 2 0 10 1 51.82 58.81 1.7644 14 2 4 2 52.06 31.32 1.7567 0 4 0 2 54.35 1.26 1.6880 14 2 5 2 56.04 1.90 1.6409 8 0 10 1 56.11 3.34 1.6391 -13 3 4 2 56.18 1.27 1.6372 1 3 8 2 56.57 13.67 1.6269 -18 0 6 1 56.75 26.85 1.6222 -4 2 10 2 56.90 1.15 1.6184 -14 2 7 2 60.15 14.19 1.5383 -14 2 8 2 60.18 8.16 1.5376 0 0 12 1 60.64 1.94 1.5271 18 0 6 1 60.91 3.22 1.5209 10 4 2 2 61.30 1.45 1.5121 8 4 4 2 62.02 1.17 1.4964 -20 2 1 2 62.33 14.18 1.4896 -20 2 2 2 62.47 18.12 1.4868 8 2 10 2 62.54 4.40 1.4853 16 0 8 1 62.62 17.34 1.4836 -6 4 6 2 62.76 10.93 1.4804 12 4 0 2 63.10 1.70 1.4734 -20 2 3 2 63.56 4.35 1.4639 22 0 2 1 63.91 11.19 1.4566 6 4 6 2 64.16 1.39 1.4516 -1 3 10 2 65.48 1.02 1.4255 -9 1 12 2 67.64 6.40 1.3851 -12 0 12 1 68.21 1.59 1.3749 24 0 0 1 68.59 3.13 1.3681 4 4 8 2 71.34 1.27 1.3221 -16 2 10 2 72.56 1.02 1.3028 12 0 12 1 72.69 2.06 1.3008 -16 4 4 2 79.57 1.61 1.2047 -8 2 14 2 80.37 2.29 1.1947 10 0 14 1 80.46 5.09 1.1937 -18 4 6 2 83.13 1.72 1.1620 -28 0 4 1 83.56 5.16 1.1570 0 4 12 2 83.96 1.23 1.1525 18 4 6 2 84.28 1.16 1.1491 4 6 2 2 85.37 3.41 1.1371 26 2 4 2 85.64 3.58 1.1342 16 4 8 2 85.93 4.16 1.1311 2 6 4 2 86.46 3.75 1.1256 20 2 10 2 86.55 3.31 1.1246 22 4 2 2 86.90 4.24 1.1210 -8 6 2 2 89.96 3.71 1.0906 -26 2 8 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.