Downeyite
      Stahl K, Legros J P, Galy J
      Zeitschrift fur Kristallographie 202 (1992) 99-107
      The crystal structure of SeO2 at 139 and 286 K
      Note: T = 139 K
      Locality: synthetic
      _database_code_amcsd 0011027

      CELL PARAMETERS:    8.3218   8.3218   5.0541   90.000   90.000   90.000
      SPACE GROUP: P4_2/mbc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    350.008
      Density (g/cm3):      4.211
      MAX. ABS. INTENSITY / VOLUME**2:      58.22418825    
      RIR:      4.502
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                15.06         12.16        5.8844    1   1   0         4
                21.35         47.27        4.1609    2   0   0         4
                23.91         51.76        3.7216    2   1   0         8
                27.77         51.37        3.2123    2   0   1         8
                29.81        100.00        2.9968    2   1   1        16
                34.07          9.17        2.6316    3   1   0         8
                35.52         23.70        2.5271    0   0   2         2
                38.57          8.78        2.3341    3   1   1        16
                38.78          8.50        2.3220    1   1   2         8
                39.03          7.17        2.3081    3   2   0         8
                41.82         11.67        2.1599    2   0   2         8
                43.09          8.30        2.0995    3   2   1        16
                43.28          1.66        2.0906    2   1   2        16
                43.50          4.88        2.0805    4   0   0         4
                46.29          2.59        1.9615    3   3   0         4
                47.25         20.29        1.9238    4   0   1         8
                48.57         16.93        1.8744    4   1   1        16
                48.95          5.66        1.8608    4   2   0         8
                50.04         16.88        1.8227    3   1   2        16
                52.40         13.07        1.7462    4   2   1        16
                53.79         14.62        1.7042    3   2   2        16
                55.19          1.44        1.6644    4   3   0         8
                56.38          2.75        1.6320    5   1   0         8
                59.17          4.74        1.5616    2   0   3         8
                59.52          7.60        1.5531    5   1   1        16
                59.67          7.29        1.5495    3   3   2         8
                59.85          1.87        1.5453    5   2   0         8
                60.30         13.24        1.5348    2   1   3        16
                61.93          4.16        1.4984    4   2   2        16
                63.21          1.11        1.4711    4   4   0         4
                65.82          1.30        1.4189    3   1   3        16
                67.37          2.37        1.3900    4   3   2        16
                68.29          7.75        1.3735    5   3   1        16
                68.43          1.68        1.3710    5   1   2        16
                68.60         11.93        1.3681    6   1   0         8
                69.02          1.69        1.3608    3   2   3        16
                71.57          7.43        1.3184    5   2   2        16
                72.15          5.45        1.3093    4   0   3         8
                72.77          1.48        1.2996    5   4   0         8
                73.18          4.42        1.2934    4   1   3        16
                74.66          3.97        1.2714    4   4   2         8
                75.20          3.86        1.2635    0   0   4         2
                75.54          3.85        1.2587    5   4   1        16
                76.24          3.95        1.2489    4   2   3        16
                79.23          2.04        1.2090    2   0   4         8
                79.57          6.15        1.2048    6   3   1        16
                79.70          9.64        1.2031    6   1   2        16
                80.23          2.27        1.1964    2   1   4        16
                82.24          2.69        1.1722    5   1   3        16
                83.68          2.91        1.1558    5   4   2        16
                84.53          2.23        1.1462    7   1   1        16
                85.19          1.26        1.1390    3   1   4        16
                88.15          1.79        1.1083    3   2   4        16
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.