Huanzalaite Macavei J, Schulz H Zeitschrift fur Kristallographie 207 (1993) 193-208 The crystal structure of wolframite type tungstates at high pressure Locality: synthetic Note: P = 4.86 GPa _database_code_amcsd 0011049 CELL PARAMETERS: 4.6360 5.6123 4.8890 90.000 90.570 90.000 SPACE GROUP: P2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 127.199 Density (g/cm3): 7.104 MAX. ABS. INTENSITY / VOLUME**2: 126.0714237 RIR: 5.778 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.79 24.03 5.6123 0 1 0 2 19.15 100.00 4.6358 1 0 0 2 24.14 99.78 3.6863 0 1 1 4 24.91 35.58 3.5742 1 1 0 4 30.88 85.30 2.8959 -1 1 1 4 31.11 83.42 2.8748 1 1 1 4 31.89 17.63 2.8061 0 2 0 2 36.77 23.47 2.4444 0 0 2 2 36.93 23.82 2.4337 0 2 1 4 37.46 16.55 2.4006 1 2 0 4 38.85 14.02 2.3179 2 0 0 2 40.24 3.36 2.2410 0 1 2 4 41.60 22.86 2.1711 -1 0 2 2 41.84 4.06 2.1592 -1 2 1 4 41.96 5.63 2.1534 1 0 2 2 42.02 28.69 2.1504 1 2 1 4 42.18 4.07 2.1424 2 1 0 4 44.76 5.50 2.0249 -1 1 2 4 45.10 6.57 2.0105 1 1 2 4 46.10 14.30 1.9689 -2 1 1 4 46.43 16.86 1.9556 2 1 1 4 48.67 6.95 1.8708 0 3 0 2 49.45 12.89 1.8432 0 2 2 4 51.11 12.13 1.7871 2 2 0 4 52.36 1.44 1.7472 0 3 1 4 52.77 21.60 1.7348 1 3 0 4 53.35 5.53 1.7172 -1 2 2 4 53.65 6.81 1.7084 1 2 2 4 54.27 13.88 1.6904 -2 0 2 2 54.54 14.88 1.6826 -2 2 1 4 54.83 16.84 1.6743 2 2 1 4 54.85 12.35 1.6736 2 0 2 2 56.19 1.83 1.6369 -1 3 1 4 56.34 1.35 1.6330 1 3 1 4 56.89 2.44 1.6185 -2 1 2 4 57.46 1.68 1.6038 2 1 2 4 59.03 7.79 1.5650 0 1 3 4 59.85 4.04 1.5453 3 0 0 2 62.32 1.79 1.4898 3 1 0 4 62.45 12.80 1.4871 -1 1 3 4 62.52 7.01 1.4856 0 3 2 4 62.86 10.18 1.4785 1 1 3 4 63.95 7.28 1.4558 2 3 0 4 64.34 4.87 1.4479 -2 2 2 4 64.87 4.93 1.4374 2 2 2 4 65.30 9.92 1.4289 -3 1 1 4 65.69 10.15 1.4213 3 1 1 4 65.91 9.54 1.4172 -1 3 2 4 66.17 11.04 1.4123 1 3 2 4 66.33 10.55 1.4092 0 2 3 4 66.95 1.07 1.3976 -2 3 1 4 69.44 2.87 1.3536 3 2 0 4 69.56 3.27 1.3515 -1 2 3 4 69.73 9.86 1.3486 0 4 1 4 69.94 3.18 1.3451 1 2 3 4 71.97 1.76 1.3121 -3 0 2 2 72.26 4.91 1.3074 -3 2 1 4 72.56 4.59 1.3028 -2 1 3 4 72.64 1.42 1.3016 3 2 1 4 72.72 4.07 1.3003 3 0 2 2 73.01 5.89 1.2959 -1 4 1 4 73.13 4.42 1.2940 1 4 1 4 73.31 4.31 1.2913 2 1 3 4 74.23 1.75 1.2776 -3 1 2 4 74.97 1.37 1.2668 3 1 2 4 75.86 4.27 1.2542 -2 3 2 4 76.35 3.88 1.2473 2 3 2 4 78.21 2.81 1.2222 0 0 4 2 79.25 2.20 1.2088 -2 2 3 4 79.98 1.97 1.1996 2 2 3 4 80.64 5.44 1.1914 3 3 0 4 80.87 1.89 1.1886 -3 2 2 4 81.19 1.20 1.1847 -1 0 4 2 81.60 1.57 1.1798 3 2 2 4 81.68 2.72 1.1789 1 0 4 2 82.69 5.59 1.1671 -2 4 1 4 82.93 5.25 1.1643 2 4 1 4 83.39 4.01 1.1589 4 0 0 2 83.86 1.10 1.1537 1 1 4 4 86.76 1.27 1.1225 0 5 0 2 86.94 2.28 1.1205 0 2 4 4 88.18 3.14 1.1080 -4 1 1 4 88.50 3.53 1.1048 -3 1 3 4 88.66 2.50 1.1032 4 1 1 4 89.57 4.09 1.0943 3 1 3 4 89.88 1.56 1.0914 -1 2 4 4 89.93 3.26 1.0909 1 5 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.