BaZnF4 Lapasset J, Bordallo H, Almairac R, Nouet J Zeitschrift fur Kristallographie 211 (1996) 934-935 Redetermination of the crystal structure of barium tetrafluorozincate, BaZnF4, at 295 K and 113 K Note: T = 295 K _database_code_amcsd 0011068 CELL PARAMETERS: 4.1974 14.5460 5.8391 90.000 90.000 90.000 SPACE GROUP: Cmc2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 356.508 Density (g/cm3): 5.192 MAX. ABS. INTENSITY / VOLUME**2: 78.09541555 RIR: 4.897 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.50 17.58 4.5532 0 2 1 2 24.48 38.96 3.6365 0 4 0 2 26.87 100.00 3.3183 1 1 1 4 28.12 22.77 3.1735 1 3 0 4 28.92 43.01 3.0868 0 4 1 2 30.62 28.49 2.9195 0 0 2 1 32.10 28.25 2.7883 1 3 1 4 37.08 1.13 2.4243 0 6 0 2 38.05 6.55 2.3649 1 1 2 4 39.59 22.70 2.2766 0 4 2 2 40.28 5.31 2.2390 0 6 1 2 40.78 28.38 2.2127 1 5 1 4 42.05 34.67 2.1486 1 3 2 4 43.10 27.87 2.0987 2 0 0 2 47.72 3.14 1.9060 2 2 1 4 48.41 4.26 1.8802 0 2 3 2 48.83 1.38 1.8651 0 6 2 2 48.91 13.66 1.8623 1 7 0 4 49.26 5.35 1.8498 1 5 2 4 50.19 9.81 1.8177 2 4 0 4 52.18 12.07 1.7529 1 1 3 4 52.73 16.31 1.7360 0 8 1 2 52.74 13.75 1.7356 2 4 1 4 53.39 8.62 1.7160 0 4 3 2 53.79 10.67 1.7041 2 0 2 2 55.37 8.02 1.6592 1 3 3 4 58.81 14.03 1.5701 1 7 2 4 59.95 11.53 1.5431 2 4 2 4 60.46 2.74 1.5312 2 6 1 4 61.05 1.85 1.5177 0 6 3 2 61.42 4.41 1.5095 1 5 3 4 61.48 1.04 1.5083 1 9 0 4 63.73 1.00 1.4603 1 9 1 4 63.76 4.28 1.4598 0 0 4 1 66.21 1.58 1.4115 0 10 1 2 66.80 2.80 1.4004 2 2 3 4 68.34 1.35 1.3726 1 1 4 4 69.37 5.48 1.3547 3 1 1 4 69.37 3.52 1.3547 0 4 4 2 69.99 1.48 1.3443 3 3 0 4 70.24 2.34 1.3400 1 9 2 4 70.38 11.69 1.3377 2 8 1 4 70.93 3.83 1.3287 0 8 3 2 70.94 6.08 1.3285 2 4 3 4 71.08 1.85 1.3262 1 3 4 4 72.10 2.50 1.3100 3 3 1 4 72.62 1.19 1.3020 0 10 2 2 75.36 2.97 1.2613 1 11 0 4 77.41 2.73 1.2328 1 11 1 4 77.44 3.03 1.2325 3 5 1 4 77.64 1.60 1.2298 2 6 3 4 78.30 3.97 1.2211 3 3 2 4 80.08 3.88 1.1984 2 0 4 2 80.58 1.34 1.1922 1 9 3 4 81.01 1.70 1.1869 0 12 1 2 82.33 1.43 1.1712 2 10 1 4 83.25 2.45 1.1606 3 7 0 4 83.49 3.22 1.1578 1 11 2 4 84.29 4.48 1.1489 1 7 4 4 85.27 3.59 1.1382 2 4 4 4 85.79 2.44 1.1326 3 1 3 4 86.74 4.14 1.1226 2 8 3 4 86.83 2.63 1.1217 1 1 5 4 88.34 1.33 1.1064 2 10 2 4 88.37 1.73 1.1061 3 3 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.