Eulytine Liu H, Kuo C Zeitschrift fur Kristallographie 212 (1997) 48-48 Crystal structure of bismuth(III) silicate, Bi4(SiO4)3 Locality: synthetic _database_code_amcsd 0011070 CELL PARAMETERS: 10.2867 10.2867 10.2867 90.000 90.000 90.000 SPACE GROUP: I-43d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1088.500 Density (g/cm3): 6.786 MAX. ABS. INTENSITY / VOLUME**2: 231.4555501 RIR: 11.106 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.16 100.00 4.1995 2 1 1 12 24.48 5.01 3.6369 2 2 0 12 27.42 94.31 3.2529 3 1 0 24 32.57 93.74 2.7492 3 2 1 24 34.89 14.34 2.5717 4 0 0 6 43.08 49.83 2.0998 4 2 2 12 44.93 21.36 2.0174 5 1 0 24 44.93 28.30 2.0174 4 3 1 24 48.47 1.10 1.8781 5 2 1 24 50.17 1.59 1.8184 4 4 0 12 51.82 17.80 1.7642 5 3 0 24 55.03 24.00 1.6687 5 3 2 24 55.03 11.84 1.6687 6 1 1 12 56.59 12.48 1.6265 6 2 0 24 58.12 19.24 1.5873 5 4 1 24 61.10 14.98 1.5167 6 3 1 24 62.56 4.93 1.4848 4 4 4 4 64.00 13.07 1.4548 5 4 3 24 64.00 6.12 1.4548 7 1 0 24 66.83 6.37 1.3998 5 5 2 12 68.23 4.51 1.3746 6 4 2 24 69.61 2.24 1.3507 7 3 0 24 72.33 5.71 1.3064 7 3 2 24 75.01 9.05 1.2662 7 4 1 24 77.66 5.64 1.2295 6 5 3 24 78.98 8.10 1.2123 6 6 0 12 78.98 8.42 1.2123 8 2 2 12 80.28 7.58 1.1958 7 4 3 24 80.28 5.28 1.1958 8 3 1 24 82.89 6.66 1.1647 7 5 2 24 84.18 1.36 1.1501 8 4 0 24 85.47 2.77 1.1360 9 1 0 24 88.05 6.09 1.1092 9 2 1 24 88.05 2.62 1.1092 6 5 5 12 89.34 3.32 1.0966 6 6 4 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.