LiCrSi2O6 Redhammer G J, Roth G Zeitschrift fur Kristallographie 219 (2004) 278-294 Structural variation and crystal chemistry of LiMe3+Si2O6 clinopyroxenes Me3+ = Al, Ga, Cr, V, Fe, Sc, and In Sample: LiCr Sample: T = 335 K _database_code_amcsd 0011111 CELL PARAMETERS: 9.5700 8.5820 5.2680 90.000 110.180 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 406.100 Density (g/cm3): 3.452 MAX. ABS. INTENSITY / VOLUME**2: 15.01866674 RIR: 1.417 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.27 57.80 6.2052 1 1 0 4 20.12 34.04 4.4135 -1 1 1 4 20.70 39.98 4.2910 0 2 0 2 25.57 34.55 3.4835 1 1 1 4 27.52 5.35 3.2408 0 2 1 4 30.14 100.00 2.9654 -2 2 1 4 30.90 1.90 2.8937 -3 1 1 4 31.65 66.02 2.8271 3 1 0 4 32.86 6.12 2.7258 1 3 0 4 34.87 1.91 2.5731 -2 0 2 2 35.75 3.45 2.5117 -1 1 2 4 35.92 15.38 2.5003 -1 3 1 4 36.34 34.33 2.4723 0 0 2 2 37.72 22.84 2.3846 2 2 1 4 39.38 1.24 2.2880 1 3 1 4 39.86 1.23 2.2615 -3 1 2 4 40.90 3.59 2.2067 -2 2 2 4 42.46 18.84 2.1289 1 1 2 4 43.20 16.29 2.0941 -3 3 1 4 43.53 6.79 2.0789 -4 2 1 4 43.77 1.05 2.0684 3 3 0 4 44.15 6.85 2.0514 -4 0 2 2 46.12 2.48 1.9682 0 4 1 4 47.72 3.30 1.9058 2 0 2 2 47.84 17.79 1.9012 -2 4 1 4 48.76 6.77 1.8678 -5 1 1 4 49.23 4.18 1.8508 -4 2 2 4 50.32 2.02 1.8133 -3 3 2 4 53.32 3.61 1.7181 2 4 1 4 54.42 5.81 1.6859 1 5 0 4 54.74 2.77 1.6768 4 2 1 4 56.65 16.06 1.6248 -2 2 3 4 56.82 7.10 1.6204 0 4 2 4 56.91 9.04 1.6181 3 1 2 4 57.91 2.32 1.5925 -4 4 1 4 57.98 17.53 1.5906 -5 3 1 4 59.60 6.01 1.5513 4 4 0 4 60.21 3.28 1.5369 -6 0 2 2 61.56 2.79 1.5064 1 1 3 4 61.66 1.86 1.5042 5 1 1 4 61.99 3.00 1.4971 6 0 0 2 62.14 1.04 1.4937 -6 2 1 4 62.36 3.78 1.4891 3 5 0 4 62.66 1.38 1.4827 -4 4 2 4 62.75 8.12 1.4807 -1 3 3 4 62.94 3.18 1.4768 -5 1 3 4 63.21 2.19 1.4712 -3 3 3 4 65.03 1.94 1.4342 4 0 2 2 65.23 6.30 1.4303 0 6 0 2 67.44 1.29 1.3887 4 4 1 4 67.65 6.42 1.3849 -3 5 2 4 69.05 2.28 1.3602 4 2 2 4 69.14 6.41 1.3587 -2 4 3 4 69.69 1.72 1.3493 1 3 3 4 69.79 14.03 1.3476 5 3 1 4 70.84 2.46 1.3301 2 2 3 4 70.97 9.02 1.3280 -7 1 2 4 70.98 2.90 1.3279 -5 3 3 4 72.84 3.64 1.2984 -3 1 4 4 73.63 3.57 1.2865 -4 0 4 2 74.81 2.22 1.2691 7 1 0 4 76.14 1.34 1.2502 -2 6 2 4 77.02 8.51 1.2381 0 6 2 4 77.17 1.66 1.2362 0 0 4 2 78.79 1.13 1.2147 1 7 0 4 80.87 5.32 1.1886 3 5 2 4 82.24 1.96 1.1722 -6 0 4 2 82.68 1.05 1.1671 1 7 1 4 89.93 2.03 1.0909 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.