LiFe.82Sc.18Si2O6 Redhammer G J, Roth G Zeitschrift fur Kristallographie 219 (2004) 278-294 Structural variation and crystal chemistry of LiMe3+Si2O6 clinopyroxenes Me3+ = Al, Ga, Cr, V, Fe, Sc, and In Sample: ScFe75 _database_code_amcsd 0011115 CELL PARAMETERS: 9.6860 8.7180 5.3080 90.000 110.200 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 420.652 Density (g/cm3): 3.366 MAX. ABS. INTENSITY / VOLUME**2: 16.53982637 RIR: 1.600 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.08 50.52 6.2920 1 1 0 4 19.91 33.33 4.4585 -1 1 1 4 20.37 30.07 4.3590 0 2 0 2 25.32 37.08 3.5178 1 1 1 4 27.18 3.47 3.2804 0 2 1 4 28.37 1.47 3.1460 2 2 0 4 29.74 100.00 3.0038 -2 2 1 4 31.25 60.07 2.8621 3 1 0 4 32.34 10.26 2.7680 1 3 0 4 34.58 1.50 2.5942 -2 0 2 2 35.40 13.42 2.5354 -1 3 1 4 35.45 3.83 2.5323 -1 1 2 4 36.06 32.35 2.4908 0 0 2 2 37.27 23.53 2.4124 2 2 1 4 38.85 1.20 2.3183 1 3 1 4 40.46 2.26 2.2293 -2 2 2 4 41.43 1.61 2.1795 0 4 0 2 42.09 16.47 2.1469 1 1 2 4 42.59 16.59 2.1230 -3 3 1 4 42.95 7.36 2.1056 -4 2 1 4 43.67 7.67 2.0725 -4 0 2 2 45.42 3.64 1.9968 0 4 1 4 46.19 1.32 1.9652 2 4 0 4 47.11 14.16 1.9291 -2 4 1 4 47.28 3.64 1.9224 2 0 2 2 48.13 7.39 1.8907 -5 1 1 4 48.65 2.88 1.8717 -4 2 2 4 49.69 3.49 1.8349 -3 3 2 4 52.55 2.85 1.7415 2 4 1 4 53.51 7.06 1.7124 1 5 0 4 54.06 3.65 1.6962 4 2 1 4 56.07 8.63 1.6402 0 4 2 4 56.11 17.60 1.6391 -2 2 3 4 56.32 8.89 1.6335 3 1 2 4 57.03 1.12 1.6149 -4 4 1 4 57.15 16.57 1.6116 -5 3 1 4 58.69 7.95 1.5730 4 4 0 4 59.46 2.95 1.5545 -6 0 2 2 60.91 2.17 1.5210 5 1 1 4 60.92 1.03 1.5208 -3 5 1 4 61.02 3.20 1.5185 1 1 3 4 61.17 3.21 1.5150 6 0 0 2 61.28 1.63 1.5126 -6 2 1 4 61.34 3.63 1.5113 3 5 0 4 61.77 2.50 1.5019 -4 4 2 4 62.09 7.23 1.4950 -1 3 3 4 62.25 3.58 1.4913 -5 1 3 4 62.49 2.71 1.4862 -3 3 3 4 63.94 1.47 1.4560 -1 5 2 4 64.09 5.92 1.4530 0 6 0 2 64.33 1.96 1.4482 4 0 2 2 66.63 6.01 1.4037 -3 5 2 4 68.24 1.79 1.3743 4 2 2 4 68.29 5.64 1.3735 -2 4 3 4 68.42 1.42 1.3712 -2 6 1 4 68.83 14.50 1.3640 5 3 1 4 68.94 2.01 1.3622 1 3 3 4 70.02 9.27 1.3437 -7 1 2 4 70.10 2.71 1.3425 -5 3 3 4 70.12 2.45 1.3421 2 2 3 4 72.18 2.98 1.3088 -3 1 4 4 72.93 4.52 1.2971 -4 0 4 2 73.77 2.49 1.2844 7 1 0 4 74.76 1.29 1.2699 6 2 1 4 74.91 2.03 1.2677 -2 6 2 4 75.06 1.15 1.2656 -6 4 2 4 75.79 8.11 1.2551 0 6 2 4 76.49 1.60 1.2454 0 0 4 2 79.07 1.30 1.2110 -1 7 1 4 79.68 5.81 1.2034 3 5 2 4 81.18 1.79 1.1848 1 7 1 4 81.32 1.69 1.1831 -6 0 4 2 83.46 1.42 1.1582 -8 2 1 4 88.81 1.44 1.1018 -8 2 3 4 88.81 2.46 1.1017 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.