LiSc.61Fe.39Si2O6 Redhammer G J, Roth G Zeitschrift fur Kristallographie 219 (2004) 278-294 Structural variation and crystal chemistry of LiMe3+Si2O6 clinopyroxenes Me3+ = Al, Ga, Cr, V, Fe, Sc, and In Sample: ScFe40 _database_code_amcsd 0011118 CELL PARAMETERS: 9.7470 8.8460 5.3350 90.000 110.280 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 431.479 Density (g/cm3): 3.205 MAX. ABS. INTENSITY / VOLUME**2: 14.29437389 RIR: 1.452 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.93 37.14 6.3574 1 1 0 4 19.76 28.06 4.4936 -1 1 1 4 20.08 31.75 4.4230 0 2 0 2 25.16 38.20 3.5394 1 1 1 4 26.90 7.90 3.3141 0 2 1 4 28.07 3.03 3.1787 2 2 0 4 29.43 100.00 3.0345 -2 2 1 4 30.30 1.22 2.9498 -3 1 1 4 31.04 59.91 2.8814 3 1 0 4 31.89 10.17 2.8063 1 3 0 4 34.38 2.95 2.6084 -2 0 2 2 34.95 12.41 2.5670 -1 3 1 4 35.24 3.61 2.5469 -1 1 2 4 35.89 30.17 2.5021 0 0 2 2 36.98 21.81 2.4311 2 2 1 4 40.13 2.04 2.2468 -2 2 2 4 40.80 1.14 2.2115 0 4 0 2 41.87 14.02 2.1578 1 1 2 4 42.11 15.83 2.1459 -3 3 1 4 42.58 6.82 2.1231 -4 2 1 4 43.39 7.62 2.0855 -4 0 2 2 44.81 4.89 2.0228 0 4 1 4 45.57 1.03 1.9908 2 4 0 4 46.48 13.07 1.9538 -2 4 1 4 47.06 3.74 1.9310 2 0 2 2 47.79 6.74 1.9034 -5 1 1 4 48.25 2.50 1.8863 -4 2 2 4 49.19 3.90 1.8522 -3 3 2 4 51.00 1.09 1.7907 5 1 0 4 51.65 1.43 1.7697 2 2 2 4 51.93 2.93 1.7608 2 4 1 4 52.70 6.71 1.7370 1 5 0 4 53.68 3.86 1.7073 4 2 1 4 55.45 8.50 1.6570 0 4 2 4 55.72 17.63 1.6497 -2 2 3 4 56.02 8.29 1.6416 3 1 2 4 56.61 15.16 1.6259 -5 3 1 4 58.03 7.48 1.5893 4 4 0 4 59.05 2.63 1.5644 -6 0 2 2 60.08 1.36 1.5401 -3 5 1 4 60.51 2.72 1.5301 3 5 0 4 60.54 1.86 1.5294 5 1 1 4 60.70 2.77 1.5257 1 1 3 4 60.78 3.15 1.5238 6 0 0 2 60.80 1.10 1.5235 -6 2 1 4 61.07 2.17 1.5173 -4 4 2 4 61.58 5.99 1.5060 -1 3 3 4 61.82 3.47 1.5008 -5 1 3 4 61.95 2.48 1.4979 -3 3 3 4 63.05 5.93 1.4743 0 6 0 2 63.12 1.31 1.4730 -1 5 2 4 63.99 1.45 1.4550 4 0 2 2 65.77 4.78 1.4200 -3 5 2 4 67.37 1.29 1.3900 -2 6 1 4 67.61 5.36 1.3857 -2 4 3 4 67.80 1.29 1.3822 4 2 2 4 68.27 14.44 1.3739 5 3 1 4 68.42 2.00 1.3713 1 3 3 4 69.47 2.15 1.3531 -5 3 3 4 69.49 8.69 1.3526 -7 1 2 4 69.69 1.59 1.3493 2 2 3 4 70.87 1.12 1.3297 -2 0 4 2 71.73 2.22 1.3159 -3 1 4 4 72.47 4.68 1.3042 -4 0 4 2 73.26 2.22 1.2921 7 1 0 4 73.83 2.77 1.2835 -2 6 2 4 74.73 7.54 1.2702 0 6 2 4 75.81 1.02 1.2548 -7 3 1 4 76.08 1.17 1.2511 0 0 4 2 78.79 5.28 1.2147 3 5 2 4 79.86 1.76 1.2011 1 7 1 4 80.74 1.26 1.1902 -6 0 4 2 82.77 1.17 1.1660 -8 2 1 4 88.04 1.21 1.1094 -8 2 3 4 88.12 2.22 1.1086 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.