CdSb Wyckoff R W G Crystal Structures 1 (1963) 85-237 Second edition. Interscience Publishers, New York, New York _database_code_amcsd 0011559 CELL PARAMETERS: 6.4710 8.2530 8.5260 90.000 90.000 90.000 SPACE GROUP: Pbca X-RAY WAVELENGTH: 1.541838 Cell Volume: 455.332 Density (g/cm3): 6.831 MAX. ABS. INTENSITY / VOLUME**2: 122.3197512 RIR: 5.831 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.84 1.89 4.2630 0 0 2 2 21.53 26.71 4.1265 0 2 0 2 23.96 3.09 3.7143 0 2 1 4 25.01 17.57 3.5599 1 0 2 4 27.28 100.00 3.2688 1 1 2 8 27.57 13.49 3.2355 2 0 0 2 27.69 48.53 3.2214 1 2 1 8 31.50 56.33 2.8402 2 1 1 8 33.24 13.59 2.6955 1 2 2 8 36.20 3.10 2.4817 1 1 3 8 36.84 22.37 2.4397 2 2 1 8 37.04 13.25 2.4270 1 3 1 8 41.01 8.10 2.2010 1 2 3 8 41.48 66.82 2.1768 1 3 2 8 42.41 29.90 2.1315 0 0 4 2 43.16 5.52 2.0958 2 3 0 4 43.79 33.95 2.0672 2 1 3 8 43.88 10.73 2.0633 0 4 0 2 44.71 24.47 2.0271 3 1 1 8 44.77 1.62 2.0245 1 0 4 4 45.22 3.66 2.0054 0 4 1 4 47.46 8.69 1.9155 1 4 1 8 47.97 9.33 1.8964 2 2 3 8 48.04 4.69 1.8938 0 2 4 4 48.13 5.45 1.8904 1 3 3 8 48.40 1.10 1.8808 2 3 2 8 48.82 14.76 1.8653 3 2 1 8 51.33 4.26 1.7800 2 0 4 4 52.46 1.35 1.7443 3 2 2 8 52.61 4.98 1.7396 2 4 0 4 54.56 7.19 1.6821 3 1 3 8 55.00 4.48 1.6696 0 4 3 4 56.96 1.69 1.6167 1 4 3 8 58.10 2.93 1.5875 4 1 0 4 58.16 6.14 1.5862 3 2 3 8 58.53 1.13 1.5770 3 3 2 8 58.57 1.65 1.5759 0 2 5 4 60.46 5.85 1.5312 1 2 5 8 61.57 1.60 1.5061 4 2 0 4 62.11 2.45 1.4944 2 3 4 8 62.60 2.37 1.4839 2 1 5 8 62.63 5.73 1.4832 4 2 1 8 62.67 6.13 1.4825 0 4 4 4 63.24 4.97 1.4703 2 5 0 4 63.32 2.16 1.4687 3 4 1 8 64.29 4.12 1.4489 2 5 1 8 65.93 3.22 1.4168 2 2 5 8 66.06 1.91 1.4143 1 3 5 8 66.43 2.37 1.4074 3 4 2 8 67.12 3.16 1.3945 4 3 0 4 68.14 1.19 1.3762 4 3 1 8 68.18 2.22 1.3755 0 6 0 2 68.56 4.85 1.3687 1 1 6 8 69.18 2.81 1.3579 0 6 1 4 69.78 3.69 1.3477 2 4 4 8 70.80 5.67 1.3308 4 2 3 8 71.44 6.33 1.3205 3 1 5 8 72.36 4.02 1.3059 2 5 3 8 73.03 3.38 1.2956 3 5 1 8 73.52 2.96 1.2881 1 4 5 8 73.86 2.04 1.2831 1 6 2 8 74.53 2.36 1.2732 4 1 4 8 74.58 3.79 1.2725 3 2 5 8 75.51 2.01 1.2591 4 4 1 8 75.95 4.76 1.2529 3 5 2 8 76.00 1.32 1.2521 2 6 1 8 76.94 6.89 1.2392 1 3 6 8 77.00 7.59 1.2384 5 0 2 4 77.02 2.23 1.2381 0 6 3 4 77.62 1.20 1.2300 4 2 4 8 79.13 4.05 1.2103 2 5 4 8 80.73 1.59 1.1903 3 5 3 8 81.08 1.52 1.1861 5 2 2 8 81.91 1.50 1.1761 2 3 6 8 82.70 2.98 1.1669 4 3 4 8 83.14 2.87 1.1618 4 4 3 8 83.68 1.96 1.1557 0 6 4 4 84.25 2.40 1.1493 1 7 1 8 86.11 4.13 1.1292 2 1 7 8 86.76 1.11 1.1224 3 4 5 8 87.07 2.03 1.1192 1 7 2 8 89.12 1.06 1.0988 2 2 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.