NiBr2 Wyckoff R W G Crystal Structures 1 (1963) 239-444 Second edition. Interscience Publishers, New York, New York Note: cadmium chloride structure _database_code_amcsd 0011810 CELL PARAMETERS: 3.7080 3.7080 18.3000 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 217.902 Density (g/cm3): 4.995 MAX. ABS. INTENSITY / VOLUME**2: 134.1417980 RIR: 8.745 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.52 36.55 6.1000 0 0 3 2 28.21 12.01 3.1629 1 0 1 6 29.28 8.90 3.0500 0 0 6 2 29.48 27.65 3.0300 0 1 2 6 34.11 100.00 2.6284 1 0 4 6 37.25 2.43 2.4138 0 1 5 6 44.70 8.73 2.0274 1 0 7 6 48.88 31.72 1.8631 0 1 8 6 49.14 32.62 1.8540 1 1 0 6 51.52 7.02 1.7739 1 1 3 12 57.63 1.33 1.5995 0 2 1 6 58.01 2.87 1.5899 1 0 10 6 58.24 6.32 1.5843 1 1 6 12 58.35 3.31 1.5814 2 0 2 6 60.73 4.78 1.5250 0 0 12 2 61.17 15.32 1.5150 0 2 4 6 62.92 3.91 1.4772 0 1 11 6 68.59 2.02 1.3682 0 2 7 6 71.83 8.51 1.3142 2 0 8 6 79.40 1.05 1.2069 0 2 10 6 81.77 10.58 1.1778 1 1 12 12 82.16 3.81 1.1731 2 1 4 12 83.72 1.50 1.1553 2 0 11 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.