HgCl2 Wyckoff R W G Crystal Structures 1 (1963) 306-307 Second edition. Interscience Publishers, New York, New York _database_code_amcsd 0011891 CELL PARAMETERS: 4.3250 12.7350 5.9630 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 328.435 Density (g/cm3): 5.490 MAX. ABS. INTENSITY / VOLUME**2: 188.9417772 RIR: 11.206 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.40 100.00 4.3525 0 2 1 4 21.70 33.22 4.0953 1 1 0 4 24.89 6.28 3.5777 1 2 0 4 25.44 3.43 3.5011 1 0 1 4 26.40 30.40 3.3758 1 1 1 8 28.03 9.49 3.1837 0 4 0 2 29.11 6.83 3.0679 1 2 1 8 29.48 24.46 3.0296 1 3 0 4 29.97 37.66 2.9815 0 0 2 2 33.17 40.53 2.7010 1 3 1 8 37.31 16.57 2.4104 1 1 2 8 38.21 5.80 2.3555 1 4 1 8 39.34 3.67 2.2904 1 2 2 8 41.13 7.84 2.1947 1 5 0 4 41.49 7.09 2.1762 0 4 2 4 41.77 4.39 2.1625 2 0 0 2 42.40 1.02 2.1320 2 1 0 4 42.54 17.18 2.1250 1 3 2 8 43.96 18.44 2.0596 1 5 1 8 45.17 6.91 2.0075 2 1 1 8 45.35 13.77 1.9996 0 6 1 4 46.92 14.65 1.9366 2 2 1 8 47.17 3.33 1.9269 2 3 0 4 47.95 10.02 1.8974 0 2 3 4 49.73 2.05 1.8335 2 3 1 8 51.06 6.45 1.7889 2 4 0 4 51.08 5.03 1.7882 1 1 3 8 51.72 7.67 1.7675 1 5 2 8 52.26 4.42 1.7505 2 0 2 4 52.79 1.09 1.7342 2 1 2 8 54.74 2.60 1.6770 1 7 0 4 55.28 8.33 1.6619 1 3 3 8 55.76 2.20 1.6485 2 5 0 4 56.90 3.56 1.6183 2 3 2 8 57.05 3.02 1.6143 1 7 1 8 57.39 1.07 1.6055 1 6 2 8 57.93 4.81 1.5919 0 8 0 2 58.78 1.46 1.5709 1 4 3 8 60.34 7.43 1.5339 2 4 2 8 62.28 3.81 1.4907 0 0 4 2 63.10 5.62 1.4733 1 5 3 8 63.35 5.38 1.4681 2 6 1 8 63.67 3.17 1.4616 1 7 2 8 64.05 2.16 1.4538 2 1 3 8 64.20 4.43 1.4508 0 6 3 4 64.60 2.66 1.4426 2 5 2 8 65.12 1.14 1.4325 3 1 0 4 65.44 4.94 1.4262 2 2 3 8 66.50 2.25 1.4061 3 2 0 4 66.60 5.98 1.4043 0 8 2 4 66.75 3.78 1.4013 3 0 1 4 66.78 2.69 1.4008 1 1 4 8 67.21 1.36 1.3929 3 1 1 8 69.31 1.55 1.3557 2 7 1 8 69.64 1.47 1.3501 0 4 4 4 69.95 1.15 1.3449 1 9 0 4 70.39 3.32 1.3376 1 3 4 8 71.98 1.96 1.3119 1 9 1 8 73.32 1.54 1.2912 3 1 2 8 73.89 1.72 1.2826 3 4 1 8 73.93 1.41 1.2820 2 8 0 4 73.95 1.30 1.2817 1 7 3 8 74.63 3.09 1.2717 3 2 2 8 76.49 1.88 1.2454 0 10 1 4 77.39 2.04 1.2332 1 5 4 8 77.82 1.21 1.2274 2 0 4 4 77.93 1.63 1.2259 1 9 2 8 79.57 2.58 1.2048 2 6 3 8 80.55 1.39 1.1926 3 6 0 4 81.66 1.09 1.1791 2 3 4 8 81.78 2.08 1.1777 2 8 2 8 82.24 1.76 1.1722 0 2 5 4 82.69 1.92 1.1670 3 0 3 4 84.62 2.54 1.1452 2 4 4 8 84.64 1.02 1.1450 1 1 5 8 87.15 1.03 1.1184 1 11 0 4 87.57 1.19 1.1142 1 7 4 8 87.60 1.11 1.1139 1 9 3 8 88.01 1.91 1.1097 1 3 5 8 88.25 2.18 1.1073 3 6 2 8 88.41 1.02 1.1057 2 5 4 8 89.07 1.71 1.0992 1 11 1 8 89.43 1.00 1.0957 3 4 3 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.