Ba2 Cu3 O7.34 Y Torardi C, McCarron E, Subramanian M, Horowitz H, Michel J, Sleight A, Cox D American Chemical Society: Symposium Series 351 (1987) 152-163 Structure-Property Relationships for RBa2Cu3Ox Phases _cod_database_code 1001432 _database_code_amcsd 0011984 CELL PARAMETERS: 3.8657 3.8657 11.6015 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 173.369 Density (g/cm3): 6.432 MAX. ABS. INTENSITY / VOLUME**2: 160.9120662 RIR: 8.146 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.62 1.19 11.6015 0 0 1 2 15.27 1.69 5.8007 0 0 2 2 23.00 2.37 3.8672 0 0 3 2 23.01 5.56 3.8657 1 0 0 4 27.73 9.71 3.2168 1 0 2 8 32.76 100.00 2.7340 1 0 3 8 32.76 53.08 2.7335 1 1 0 4 36.33 2.66 2.4727 1 1 2 8 38.81 6.60 2.3203 0 0 5 2 38.82 7.48 2.3200 1 0 4 8 40.41 11.15 2.2321 1 1 3 8 46.99 7.73 1.9336 0 0 6 2 47.01 30.87 1.9329 2 0 0 4 51.67 3.74 1.7689 1 1 5 8 55.44 1.39 1.6574 0 0 7 2 55.46 2.37 1.6568 2 1 2 16 58.47 12.41 1.5786 1 1 6 8 58.48 31.72 1.5783 2 1 3 16 60.81 1.23 1.5233 1 0 7 8 62.54 4.89 1.4851 2 0 5 8 62.55 2.85 1.4850 2 1 4 16 65.91 2.19 1.4172 1 1 7 8 68.66 7.86 1.3670 2 0 6 8 68.67 7.70 1.3667 2 2 0 4 69.19 3.65 1.3578 1 0 8 8 75.58 1.83 1.2582 2 0 7 8 78.16 1.57 1.2229 1 0 9 8 78.19 5.70 1.2225 3 0 3 8 78.19 6.18 1.2224 3 1 0 8 81.78 1.84 1.1776 2 2 5 8 82.81 1.44 1.1656 3 1 3 16 87.38 3.47 1.1161 2 2 6 8 87.86 2.11 1.1112 1 0 10 8 87.87 3.32 1.1110 2 1 8 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.