As2O5 Jansen M Angewandte Chemie 89 (1977) 326-327 Kristallstruktur von As2O5 _database_code_amcsd 0011989 CELL PARAMETERS: 8.6460 8.4500 4.6260 90.000 90.000 90.000 SPACE GROUP: P2_12_12_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 337.970 Density (g/cm3): 4.516 MAX. ABS. INTENSITY / VOLUME**2: 53.76356532 RIR: 3.876 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.66 100.00 6.0432 1 1 0 4 20.54 14.98 4.3230 2 0 0 2 21.03 13.06 4.2250 0 2 0 2 21.79 4.11 4.0789 1 0 1 4 21.90 2.66 4.0577 0 1 1 4 23.11 1.77 3.8486 2 1 0 4 23.44 1.98 3.7960 1 2 0 4 24.23 43.40 3.6733 1 1 1 4 28.25 26.82 3.1585 2 0 1 4 28.61 24.46 3.1197 0 2 1 4 29.56 13.53 3.0216 2 2 0 4 30.21 35.81 2.9586 2 1 1 4 30.46 40.82 2.9345 1 2 1 4 35.49 3.95 2.5297 2 2 1 4 36.74 16.61 2.4461 3 0 1 4 37.38 11.58 2.4058 0 3 1 4 37.79 9.49 2.3808 3 2 0 4 38.13 10.55 2.3599 2 3 0 4 38.31 3.01 2.3497 3 1 1 4 41.82 15.69 2.1602 1 1 2 4 43.20 3.58 2.0941 4 1 0 4 44.13 5.00 2.0521 1 4 0 4 45.77 3.22 1.9825 2 1 2 4 45.95 3.29 1.9752 1 2 2 4 47.23 2.65 1.9243 4 2 0 4 47.67 13.07 1.9077 4 1 1 4 47.93 2.94 1.8980 2 4 0 4 48.53 14.07 1.8758 1 4 1 4 49.64 11.36 1.8367 2 2 2 4 51.43 3.65 1.7767 4 2 1 4 52.08 2.27 1.7560 2 4 1 4 54.14 1.16 1.6941 5 1 0 4 55.38 3.39 1.6590 3 2 2 4 55.39 1.52 1.6586 1 5 0 4 55.64 2.98 1.6519 2 3 2 4 59.55 5.03 1.5524 4 1 2 4 60.29 3.85 1.5351 1 4 2 4 60.99 11.40 1.5191 3 3 2 4 61.29 3.73 1.5124 5 2 1 4 61.36 2.50 1.5108 4 4 0 4 62.31 3.74 1.4901 2 5 1 4 64.12 1.76 1.4524 2 0 3 4 64.31 1.76 1.4485 0 2 3 4 64.69 1.20 1.4410 6 0 0 2 64.93 4.04 1.4361 4 4 1 4 65.17 3.11 1.4314 2 1 3 4 65.32 2.52 1.4286 1 2 3 4 65.74 3.42 1.4205 6 1 0 4 66.38 1.54 1.4083 0 6 0 2 66.60 5.41 1.4041 5 3 1 4 67.35 4.39 1.3904 3 5 1 4 67.37 3.63 1.3900 1 6 0 4 67.65 5.85 1.3850 5 0 2 4 68.06 1.25 1.3775 4 3 2 4 68.39 1.35 1.3718 3 4 2 4 68.67 1.11 1.3667 5 1 2 4 68.80 4.09 1.3646 0 5 2 4 69.08 1.76 1.3596 3 0 3 4 69.50 3.71 1.3526 0 3 3 4 69.77 1.25 1.3479 1 5 2 4 70.10 1.09 1.3424 3 1 3 4 70.47 1.72 1.3363 1 3 3 4 72.22 2.77 1.3082 6 2 1 4 73.65 2.34 1.2863 2 6 1 4 75.10 2.37 1.2649 4 4 2 4 76.76 2.16 1.2417 4 1 3 4 77.16 1.48 1.2362 6 3 1 4 77.42 2.52 1.2328 1 4 3 4 78.34 1.74 1.2205 3 6 1 4 79.26 2.36 1.2086 5 5 0 4 81.45 1.74 1.1816 7 1 1 4 83.52 1.44 1.1575 1 7 1 4 83.61 1.56 1.1565 0 0 4 2 87.94 1.05 1.1104 5 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.