NaTa3O8 Range K J, Wildenauer M, Heyns A M Angewandte Chemie 100 (1988) 973-975 Extrem kurze nichtbindende sauerstoff-sauerstoff-abstaende: Die kristallstrukturen von NbBO4, NaNb3O8 und NaTa3O8 Note: data from ICSD _database_code_amcsd 0011991 CELL PARAMETERS: 7.2420 10.4620 7.0010 90.000 90.000 90.000 SPACE GROUP: Ibam X-RAY WAVELENGTH: 1.541838 Cell Volume: 530.436 Density (g/cm3): 8.687 MAX. ABS. INTENSITY / VOLUME**2: 229.3163860 RIR: 8.595 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.88 57.51 5.9546 1 1 0 4 16.95 17.29 5.2310 0 2 0 2 24.54 4.61 3.6270 1 2 1 8 24.58 7.70 3.6210 2 0 0 2 25.45 7.14 3.5005 0 0 2 2 28.41 11.07 3.1420 1 3 0 4 29.05 1.94 3.0743 2 1 1 8 29.60 17.73 3.0177 1 1 2 8 30.01 100.00 2.9773 2 2 0 4 30.73 92.17 2.9092 0 2 2 4 34.29 25.59 2.6155 0 4 0 2 35.67 49.68 2.5167 2 0 2 4 38.26 1.29 2.3522 3 1 0 4 38.50 4.32 2.3382 1 3 2 8 38.80 3.30 2.3209 1 4 1 8 39.74 4.93 2.2679 2 2 2 8 42.64 1.37 2.1202 2 4 0 4 43.18 3.55 2.0952 0 4 2 4 44.30 3.51 2.0445 1 2 3 8 45.10 2.06 2.0102 1 5 0 4 45.71 6.76 1.9849 3 3 0 4 46.52 5.97 1.9524 3 1 2 8 47.14 1.37 1.9280 2 1 3 8 50.31 53.43 1.8135 2 4 2 8 50.40 12.25 1.8105 4 0 0 2 52.27 14.57 1.7502 0 0 4 2 52.49 4.49 1.7432 1 5 2 8 52.97 1.23 1.7287 4 1 1 8 53.04 3.41 1.7266 3 3 2 8 53.27 2.55 1.7196 3 4 1 8 53.56 2.06 1.7109 4 2 0 4 54.17 2.06 1.6930 1 4 3 8 54.66 3.93 1.6792 1 1 4 8 55.35 1.53 1.6598 0 2 4 4 55.80 4.99 1.6476 1 6 1 8 57.29 1.09 1.6081 4 0 2 4 58.58 1.10 1.5758 2 0 4 4 58.78 12.85 1.5710 2 6 0 4 58.98 1.22 1.5661 4 3 1 8 59.20 14.04 1.5608 0 6 2 4 60.20 30.34 1.5371 4 2 2 8 60.56 3.06 1.5290 1 3 4 8 61.45 25.78 1.5088 2 2 4 8 62.38 11.07 1.4886 4 4 0 4 64.01 10.09 1.4546 0 4 4 4 64.69 3.51 1.4409 3 5 2 8 65.00 1.18 1.4347 5 1 0 4 65.08 1.66 1.4333 2 6 2 8 65.90 1.29 1.4173 4 1 3 8 66.17 1.50 1.4122 3 4 3 8 66.60 1.11 1.4042 3 1 4 8 67.62 1.99 1.3855 3 6 1 8 68.40 1.79 1.3715 1 6 3 8 68.49 1.05 1.3699 4 4 2 8 69.62 2.87 1.3504 1 7 2 8 69.66 1.10 1.3498 2 4 4 8 71.00 2.44 1.3275 5 1 2 8 71.47 1.33 1.3200 1 5 4 8 71.92 2.66 1.3128 3 3 4 8 72.24 2.85 1.3077 0 8 0 2 75.04 3.02 1.2657 1 8 1 8 75.56 7.07 1.2584 4 0 4 4 76.19 1.16 1.2495 5 3 2 8 78.12 1.31 1.2235 4 2 4 8 79.23 1.05 1.2090 3 6 3 8 81.41 8.33 1.1821 4 6 2 8 81.91 4.82 1.1761 6 2 0 4 82.51 10.05 1.1691 2 6 4 8 83.26 8.14 1.1604 2 8 2 8 85.00 4.98 1.1411 6 0 2 4 85.21 5.37 1.1388 0 2 6 4 85.60 1.92 1.1347 3 8 1 8 85.66 9.26 1.1340 4 4 4 8 86.33 1.62 1.1269 1 8 3 8 87.92 4.80 1.1106 2 0 6 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.