Althupite Piret P, Deliens M Bulletin de Mineralogie 110 (1987) 65-72 Les phosphates d'uranyle et d'aluminium de Kobokobo IX. L'althupite AlTh(UO2)[(UO2)3O(OH)PO4)2]2(OH)3*15H2O, nouveau mineral; proprietes et structure cristalline Note: Sample is form Kobokobo, Kivu, Zaire _database_code_amcsd 0012087 10.953 18.567 13.504 72.64 68.20 84.21 P-1 atom x y z Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) U1 .5 0 .5 .0214 .0294 .0164 .0203 .0022 -.0125 -.0039 U2 .5 .5 .5 .0191 .0260 .0129 .0186 .0021 -.0059 -.0082 U3 .4393 .2473 .0280 .0187 .0296 .0110 .0150 .0016 -.0086 -.0023 U4 .5261 .0469 .1877 .0195 .0319 .0116 .0149 .0009 -.0086 -.0033 U5 .5123 .2050 .3050 .0193 .0333 .0110 .0159 .0040 -.0122 -.0043 U6 .4355 .4608 .8294 .0199 .0334 .0101 .0166 .0000 -.0106 -.0023 U7 .4342 .2935 .7127 .0175 .0282 .0099 .0156 .0038 -.0100 -.0040 U8 .1307 .3881 .3879 .0295 .0277 .0269 .0361 .0076 -.0121 -.0137 Th9 .8178 .0728 .6964 .0252 .0229 .0279 .0259 .0033 -.0073 -.0120 Al10 .017 .075 .418 .030 P11 .547 .133 .590 .016 P12 .502 .116 .901 .023 P13 .412 .389 .131 .021 P14 .452 .365 .414 .019 O15 .331 .020 .534 .040 O16 .662 .469 .482 .014 O17 .606 .276 -.052 .064 O18 .272 .224 .100 .074 O19 .348 .014 .243 .039 O20 .700 .065 .117 .093 O21 .339 .195 .391 .059 O22 .683 .217 .223 .073 O23 .274 .492 .872 .004 O24 .596 .425 .787 .000 O25 .600 .315 .685 .055 O26 .266 .274 .745 .058 O27 .101 .295 .394 .052 O28 .142 .481 .393 .036 O29 .531 .080 .331 .031 O30 .445 -.140 .530 .026 O31 .471 .060 .658 .012 O32 .498 .444 .348 .026 O33 .458 .363 .524 .034 OH34 .400 .426 .682 .025 O35 .482 .169 .173 .032 O36 .444 .306 .178 .044 O37 .404 .391 .020 .022 OH38 .372 .329 -.119 .019 O39 .437 .190 -.132 .022 O40 .494 .112 .014 .018 O41 .429 .049 -.099 .026 O42 .547 .307 .359 .024 O43 .475 .558 .887 .029 O44 .478 .200 .628 .033 O45 .691 .129 .593 .032 O46 .649 .115 .823 .033 O47 .280 .408 .215 .030 O48 .308 .350 .427 .034 Wat49 -.110 .394 .493 .050 Wat50 .019 .442 .248 .128 Wat51 .081 .344 .592 .054 Wat52 .793 .344 .900 .049 Wat53 .840 .220 .644 .058 Wat54 .982 .112 .758 .056 OH55 .961 -.033 .694 .038 OH56 .990 .122 .529 .034 OH57 .885 .005 .533 .036 Wat58 .886 .144 .373 .036 Wat59 .156 .147 .323 .026 Wat60 .133 .432 .723 .050 Wat61 .204 .194 .609 .066 Wat62 .778 .301 .420 .087 Wat63 .098 .347 .953 .130 Wat64 .868 .183 .925 .139 Wat65 .165 .666 .247 .094 Wat66 .753 .431 .938 .111