Sanidine Ohashi Y, Finger LW Carnegie Institution of Washington: Yearbook 74 (1975) 569-572 An effect of temperature on the feldspar structure: crystal structure of sanidine at 800C Note: T = 800 C Locality: Laacher See, Eifel District, Germany _database_code_amcsd 0020566 CELL PARAMETERS: 8.6820 13.0130 7.1840 90.000 115.710 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 731.289 Density (g/cm3): 2.507 MAX. ABS. INTENSITY / VOLUME**2: 5.082649929 RIR: 0.660 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.21 9.06 6.7044 1 1 0 4 13.61 15.17 6.5065 0 2 0 2 13.68 6.59 6.4728 0 0 1 2 15.08 16.97 5.8742 -1 1 1 4 20.83 71.22 4.2654 -2 0 1 2 22.36 22.02 3.9762 1 1 1 4 22.74 4.12 3.9112 2 0 0 2 23.45 88.08 3.7935 1 3 0 4 24.58 15.35 3.6221 -1 3 1 4 24.96 11.23 3.5672 -2 2 1 4 25.74 48.01 3.4617 -1 1 2 4 26.59 100.00 3.3522 2 2 0 4 27.09 53.62 3.2916 -2 0 2 2 27.42 29.05 3.2532 0 4 0 2 27.56 80.23 3.2364 0 0 2 2 29.70 54.83 3.0084 1 3 1 4 30.43 8.96 2.9371 -2 2 2 4 30.76 23.01 2.9068 0 4 1 4 30.86 11.50 2.8977 0 2 2 4 31.69 3.77 2.8234 -3 1 1 4 32.36 15.55 2.7662 -1 3 2 4 34.22 20.19 2.6203 -3 1 2 4 34.40 1.43 2.6071 2 2 1 4 34.68 30.68 2.5867 -2 4 1 4 34.98 9.05 2.5650 1 1 2 4 35.10 9.31 2.5567 3 1 0 4 35.90 5.26 2.5011 2 4 0 4 37.15 6.82 2.4203 -1 5 1 4 37.37 8.65 2.4064 -3 3 1 4 38.80 3.66 2.3209 -1 1 3 4 40.86 1.79 2.2087 1 5 1 4 41.64 19.67 2.1688 0 6 0 2 41.87 1.08 2.1576 0 0 3 2 42.07 2.27 2.1477 -4 0 1 2 42.19 7.78 2.1418 2 4 1 4 42.38 3.48 2.1327 -4 0 2 2 43.34 1.81 2.0879 2 0 2 2 44.03 3.21 2.0565 0 6 1 4 44.42 1.40 2.0395 -4 2 1 4 44.72 9.84 2.0266 -4 2 2 4 45.63 10.38 1.9881 2 2 2 4 46.37 2.18 1.9581 -3 3 3 4 46.43 8.20 1.9556 4 0 0 2 46.97 2.24 1.9347 -3 5 1 4 47.29 3.45 1.9222 -4 0 3 2 47.96 2.49 1.8967 2 6 0 4 48.61 2.52 1.8729 4 2 0 4 48.92 3.66 1.8619 1 1 3 4 49.44 2.34 1.8434 -4 2 3 4 49.48 3.65 1.8420 3 5 0 4 50.39 2.74 1.8110 -2 6 2 4 50.67 7.23 1.8017 0 6 2 4 50.78 7.06 1.7981 0 4 3 4 50.85 15.44 1.7956 -2 0 4 2 50.95 3.75 1.7923 -4 4 1 4 51.22 1.70 1.7836 -4 4 2 4 52.05 2.75 1.7572 2 4 2 4 53.06 1.45 1.7259 1 3 3 4 53.30 1.72 1.7186 -5 1 2 4 54.71 3.52 1.6776 -3 5 3 4 55.68 2.51 1.6509 -1 7 2 4 55.93 4.18 1.6440 3 5 1 4 56.11 1.99 1.6390 -5 1 3 4 56.99 1.10 1.6159 2 0 3 2 57.79 3.37 1.5955 -4 2 4 4 58.51 1.16 1.5776 0 8 1 4 58.80 3.67 1.5704 0 2 4 4 59.91 4.34 1.5440 -5 3 3 4 60.69 4.10 1.5261 -4 6 1 4 61.77 13.74 1.5019 2 8 0 4 62.56 1.59 1.4847 -5 1 4 4 63.18 2.14 1.4717 5 3 0 4 63.74 1.27 1.4600 -1 7 3 4 64.01 2.61 1.4545 1 1 4 4 64.07 1.10 1.4534 0 8 2 4 64.38 4.81 1.4472 2 4 3 4 64.43 3.47 1.4461 -6 0 2 2 64.59 2.90 1.4429 -5 5 2 4 64.81 1.15 1.4385 -4 6 3 4 65.54 1.48 1.4242 3 5 2 4 65.62 4.01 1.4227 4 0 2 2 66.76 1.38 1.4011 -6 0 1 2 67.21 1.95 1.3928 -4 0 5 2 67.54 1.19 1.3869 1 3 4 4 67.75 1.44 1.3831 -2 6 4 4 68.50 1.17 1.3697 -6 2 1 4 68.52 1.13 1.3694 -1 1 5 4 68.95 1.20 1.3620 -4 2 5 4 70.17 2.54 1.3413 -1 9 2 4 70.19 1.16 1.3409 5 5 0 4 70.39 1.51 1.3376 -6 0 4 2 71.94 2.90 1.3125 -1 3 5 4 72.10 1.24 1.3099 -5 1 5 4 72.22 1.44 1.3082 2 0 4 2 72.50 1.14 1.3037 6 0 0 2 72.82 1.45 1.2989 0 8 3 4 72.94 1.21 1.2970 0 6 4 4 72.96 1.73 1.2967 -4 8 1 4 73.18 4.52 1.2934 -4 8 2 4 73.61 1.39 1.2869 -6 4 1 4 73.85 5.51 1.2832 2 8 2 4 74.61 1.33 1.2720 -3 9 2 4 75.45 1.67 1.2599 -5 3 5 4 75.76 1.85 1.2555 -3 5 5 4 83.57 1.82 1.1569 -4 8 4 4 84.44 2.04 1.1472 0 8 4 4 85.58 1.39 1.1349 4 4 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.