Alite De la Torre A G, De Vera R N, Cuberos A J M, Aranda M A G Cement and Concrete Research 38 (2008) 1261-1269 Crystal structure of low magnesium-content alite: application to Rietveld quantitative phase analysis Locality: synthetic _database_code_amcsd 0017753 CELL PARAMETERS: 11.6389 14.1716 13.6434 104.982 94.622 90.107 SPACE GROUP: P-1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 2166.199 Density (g/cm3): 3.095 MAX. ABS. INTENSITY / VOLUME**2: 6.933754873 RIR: 0.730 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.46 2.59 13.6861 0 1 0 2 7.62 1.77 11.5978 1 0 0 2 11.36 2.60 7.7878 1 -1 1 2 12.54 3.59 7.0605 -1 1 1 2 12.94 2.09 6.8394 0 -2 1 2 14.88 1.84 5.9554 -1 2 0 2 14.90 1.01 5.9462 -1 -1 2 2 14.94 7.13 5.9316 -1 0 2 2 15.28 1.24 5.7989 2 0 0 2 16.08 2.47 5.5108 0 2 1 2 16.10 1.88 5.5052 0 -2 2 2 16.42 1.17 5.3991 0 1 2 2 17.57 1.26 5.0483 -1 1 2 2 17.95 2.20 4.9408 -2 1 1 2 21.59 1.57 4.1155 -2 1 2 2 21.78 2.19 4.0812 -1 -3 2 2 22.90 7.04 3.8828 1 2 2 2 22.91 3.98 3.8820 1 -2 3 2 24.25 1.85 3.6701 0 -3 3 2 24.66 2.08 3.6099 -3 1 1 2 25.14 2.51 3.5429 0 -4 1 2 25.23 2.18 3.5303 -2 2 2 2 25.27 1.83 3.5240 -2 -2 3 2 25.35 1.20 3.5131 -2 -3 2 2 25.74 1.46 3.4609 -3 0 2 2 26.18 1.12 3.4045 2 -3 2 2 27.30 1.08 3.2666 -3 1 2 2 29.34 35.40 3.0441 -1 4 1 2 29.39 31.47 3.0392 -1 -4 3 2 29.51 37.45 3.0265 -3 0 3 2 30.01 11.50 2.9777 -2 4 0 2 30.07 11.46 2.9720 -2 -4 2 2 30.13 11.52 2.9658 -2 0 4 2 31.94 1.44 2.8019 -4 1 1 2 32.15 100.00 2.7842 3 0 3 2 32.49 51.87 2.7554 0 4 2 2 32.53 45.61 2.7526 0 -4 4 2 32.70 41.89 2.7387 -4 0 2 2 33.21 2.59 2.6975 0 -2 5 2 33.32 1.57 2.6890 -4 -2 1 2 33.35 1.07 2.6864 4 1 1 2 33.93 1.63 2.6421 -4 1 2 2 34.30 42.75 2.6143 3 -4 1 2 34.36 47.62 2.6097 -3 -4 1 2 34.37 35.97 2.6094 -1 0 5 2 34.86 1.50 2.5738 4 0 2 2 34.93 1.13 2.5684 1 -5 3 2 35.04 2.68 2.5608 -1 -3 5 2 36.59 4.67 2.4559 3 -1 4 2 36.63 1.68 2.4531 2 5 0 2 37.39 1.63 2.4050 3 0 4 2 37.71 1.50 2.3855 -1 -4 5 2 38.24 1.02 2.3535 -3 3 3 2 38.58 1.45 2.3337 3 -3 4 2 38.64 9.63 2.3301 1 4 3 2 38.66 1.10 2.3290 4 0 3 2 38.66 8.34 2.3289 1 -4 5 2 38.85 10.49 2.3178 -5 0 1 2 39.10 2.68 2.3036 -3 4 2 2 39.19 1.18 2.2988 -3 -4 4 2 39.21 1.01 2.2976 4 3 1 2 39.23 1.41 2.2966 -3 -2 5 2 39.28 1.03 2.2936 -5 -1 1 2 39.53 1.91 2.2799 -2 -5 4 2 39.56 1.14 2.2781 5 1 0 2 40.23 1.01 2.2419 -4 -4 1 2 40.63 1.39 2.2203 4 -3 3 2 41.13 1.97 2.1944 -5 1 2 2 41.22 14.58 2.1899 4 -4 2 2 41.23 4.84 2.1897 3 -4 4 2 41.24 1.50 2.1889 1 2 5 2 41.24 18.60 2.1889 0 0 6 2 41.25 4.16 2.1884 3 4 2 2 41.26 1.74 2.1880 1 -2 6 2 41.29 12.46 2.1867 4 4 0 2 41.35 3.24 2.1833 5 -2 1 2 41.40 2.83 2.1812 5 2 0 2 41.51 3.02 2.1754 2 -6 2 2 41.56 2.77 2.1731 -2 -6 1 2 41.64 1.67 2.1690 -4 4 1 2 41.65 3.22 2.1682 -2 2 5 2 41.70 4.06 2.1661 -2 -2 6 2 41.73 2.66 2.1646 -4 -4 3 2 42.36 1.32 2.1336 -5 -1 3 2 43.08 1.19 2.0996 -1 -4 6 2 43.56 3.76 2.0779 -1 5 3 2 44.74 1.11 2.0256 -2 -4 6 2 45.09 1.19 2.0109 -2 1 6 2 45.52 1.06 1.9926 -5 -1 4 2 45.65 1.06 1.9871 -2 3 5 2 45.68 2.20 1.9862 -1 6 2 2 45.70 1.99 1.9851 -3 6 0 2 45.75 3.54 1.9833 -1 -6 5 2 45.80 1.30 1.9813 -3 -6 3 2 45.90 1.27 1.9772 -3 0 6 2 45.97 2.66 1.9742 -5 0 4 2 46.79 8.34 1.9414 2 4 4 2 46.80 9.72 1.9410 2 -4 6 2 47.01 10.14 1.9330 6 0 0 2 49.63 2.99 1.8369 0 6 3 2 49.68 1.78 1.8351 0 -6 6 2 49.71 1.00 1.8340 1 5 4 2 49.89 2.59 1.8281 1 0 7 2 49.90 2.22 1.8276 5 -4 3 2 49.95 1.31 1.8258 -6 0 3 2 49.96 2.25 1.8255 5 4 1 2 51.60 36.39 1.7714 0 -8 2 2 51.79 32.84 1.7651 -4 4 4 2 51.89 31.47 1.7620 -4 -4 6 2 55.82 2.07 1.6469 5 -6 2 2 55.90 2.11 1.6447 -1 0 8 2 55.92 1.99 1.6441 -5 -6 1 2 56.35 15.27 1.6327 3 4 5 2 56.35 14.74 1.6327 3 -4 7 2 56.57 13.13 1.6269 7 0 1 2 59.82 8.18 1.5459 2 0 8 2 59.87 7.76 1.5450 6 -4 4 2 59.93 8.32 1.5436 6 4 2 2 60.50 1.50 1.5302 -3 8 1 2 60.63 1.74 1.5274 -3 -8 5 2 60.86 1.04 1.5221 -2 8 2 2 60.97 1.01 1.5196 -2 -8 6 2 62.08 8.51 1.4950 3 -8 5 2 62.12 6.90 1.4942 3 8 1 2 62.20 8.01 1.4925 -1 4 7 2 62.27 7.56 1.4911 -1 -4 9 2 62.36 8.66 1.4890 -7 4 1 2 62.37 4.89 1.4888 -4 8 0 2 62.47 8.53 1.4867 -7 -4 3 2 62.50 5.30 1.4860 -4 -8 4 2 62.65 5.25 1.4829 -4 0 8 2 63.42 5.33 1.4666 -1 8 3 2 63.52 5.37 1.4646 -1 -8 7 2 63.86 6.48 1.4576 -7 0 5 2 64.17 1.01 1.4513 2 5 6 2 66.35 1.09 1.4088 5 -8 1 2 66.50 1.03 1.4061 -5 -8 3 2 67.25 6.13 1.3921 6 0 6 2 68.05 1.79 1.3777 0 8 4 2 68.13 2.04 1.3763 0 -8 8 2 72.28 1.37 1.3071 6 -8 2 2 72.43 1.28 1.3048 -6 -8 2 2 79.23 1.19 1.2090 9 0 3 2 80.01 2.64 1.1992 7 -8 3 2 80.11 2.41 1.1979 -1 0 11 2 80.16 2.42 1.1973 -7 -8 1 2 82.86 2.86 1.1651 2 8 6 2 82.91 2.42 1.1645 2 -8 10 2 83.40 2.38 1.1589 -10 0 2 2 85.06 2.60 1.1405 0 12 0 2 85.11 2.31 1.1399 0 -12 6 2 85.28 2.01 1.1381 -4 8 6 2 85.47 2.19 1.1360 -4 -8 10 2 85.61 1.96 1.1346 -8 4 6 2 85.74 1.64 1.1331 -8 -4 8 2 86.04 2.36 1.1300 3 -12 3 2 86.14 2.46 1.1289 -3 -12 3 2 86.35 2.49 1.1267 -7 8 3 2 86.46 1.58 1.1256 -5 4 9 2 86.57 2.56 1.1244 -7 -8 7 2 86.58 1.68 1.1243 -5 -4 11 2 89.52 2.41 1.0949 6 -8 8 2 89.56 2.09 1.0944 2 4 10 2 89.58 2.07 1.0942 6 8 4 2 89.61 2.03 1.0940 2 -4 12 2 89.85 2.53 1.0917 10 -4 2 2 89.96 2.42 1.0906 10 4 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.