UTiNb2O10 Chevalier R, Gasperin M Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences 268 (1969) 1426-1428 Synthese en monocristaux et structure cristalline de l'oxyde UTiNb2O10 _cod_database_code 1001143 _database_code_amcsd 0012277 CELL PARAMETERS: 7.2800 12.6200 16.0200 90.000 90.000 90.000 SPACE GROUP: Fddd X-RAY WAVELENGTH: 1.541838 Cell Volume: 1471.815 Density (g/cm3): 5.701 MAX. ABS. INTENSITY / VOLUME**2: 105.8866334 RIR: 6.048 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.10 40.90 5.8678 1 1 1 8 17.90 8.49 4.9567 0 2 2 4 21.81 41.11 4.0752 1 1 3 8 22.20 93.27 4.0050 0 0 4 2 25.07 10.38 3.5517 1 3 1 8 26.90 2.27 3.3139 2 0 2 4 28.29 49.19 3.1550 0 4 0 2 28.30 100.00 3.1530 2 2 0 4 29.69 16.25 3.0090 1 3 3 8 31.32 1.73 2.8564 1 1 5 8 36.25 24.05 2.4784 0 4 4 4 36.26 49.23 2.4774 2 2 4 8 36.54 1.45 2.4589 0 2 6 4 38.15 8.23 2.3587 1 5 1 8 38.18 8.26 2.3571 3 1 1 8 39.43 6.48 2.2850 2 4 2 8 41.47 11.56 2.1775 1 5 3 8 41.50 11.63 2.1762 3 1 3 8 42.00 10.29 2.1513 1 1 7 8 43.42 1.68 2.0841 3 3 1 8 45.28 16.47 2.0025 0 0 8 2 46.43 3.65 1.9559 3 3 3 8 46.89 6.50 1.9378 1 3 7 8 47.53 1.69 1.9130 1 5 5 8 47.55 1.69 1.9121 3 1 5 8 50.09 24.66 1.8212 2 6 0 4 50.12 12.12 1.8200 4 0 0 2 51.38 2.71 1.7783 2 4 6 8 52.61 1.36 1.7396 1 7 1 8 52.63 1.31 1.7390 3 5 1 8 54.26 10.36 1.6907 0 4 8 4 54.27 21.06 1.6904 2 2 8 8 55.24 2.68 1.6630 1 7 3 8 55.26 2.59 1.6624 3 5 3 8 55.42 20.92 1.6578 2 6 4 8 55.46 10.25 1.6569 4 0 4 4 55.66 5.85 1.6512 1 5 7 8 55.68 5.90 1.6506 3 1 7 8 58.51 5.89 1.5775 0 8 0 2 58.55 11.79 1.5765 4 4 0 4 59.54 1.35 1.5527 0 2 10 4 59.73 2.56 1.5481 3 3 7 8 63.37 5.26 1.4677 0 8 4 4 63.41 10.53 1.4669 4 4 4 8 65.81 3.82 1.4190 1 1 11 8 67.00 1.20 1.3968 3 7 3 8 67.04 1.17 1.3961 5 1 3 8 67.36 2.07 1.3901 1 7 7 8 67.38 2.00 1.3898 3 5 7 8 69.51 2.89 1.3523 1 3 11 8 69.81 11.87 1.3473 2 6 8 8 69.83 5.84 1.3468 4 0 8 4 70.55 1.76 1.3350 0 0 12 2 70.65 1.22 1.3333 1 9 3 8 70.70 1.26 1.3324 5 3 3 8 70.87 2.22 1.3297 2 4 10 8 75.64 1.03 1.2573 5 5 1 8 76.67 2.84 1.2429 1 5 11 8 76.69 2.86 1.2427 3 1 11 8 76.94 3.52 1.2392 0 8 8 4 76.98 7.04 1.2387 4 4 8 8 77.66 1.35 1.2295 0 4 12 4 77.67 2.76 1.2293 2 2 12 8 77.82 1.61 1.2274 5 5 3 8 78.14 1.14 1.2231 3 7 7 8 78.18 1.11 1.2227 5 1 7 8 80.18 1.65 1.1971 3 3 11 8 80.56 3.70 1.1924 2 10 0 4 80.59 3.66 1.1920 4 8 0 4 80.63 3.70 1.1915 6 2 0 4 81.26 1.12 1.1839 3 9 3 8 81.60 1.14 1.1798 1 9 7 8 81.65 1.18 1.1792 5 3 7 8 84.84 3.96 1.1428 2 10 4 8 84.87 3.90 1.1425 4 8 4 8 84.91 3.97 1.1420 6 2 4 8 87.05 1.49 1.1194 1 7 11 8 87.07 1.45 1.1192 3 5 11 8 88.52 1.47 1.1046 5 5 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.