Bi4 Ge3 O12 Durif A, Averbuch-Pouchot M Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences 295 (1982) 555-556 Affinement de la structure cristalline du germanate de bismuth Bi4 (Ge O4)3. _cod_database_code 1007142 _database_code_amcsd 0012297 CELL PARAMETERS: 10.4970 10.4970 10.4970 90.000 90.000 90.000 SPACE GROUP: I-43d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1156.633 Density (g/cm3): 7.153 MAX. ABS. INTENSITY / VOLUME**2: 245.9850208 RIR: 11.197 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.73 62.07 4.2854 2 1 1 12 26.86 99.49 3.3194 3 1 0 24 31.90 100.00 2.8054 3 2 1 24 34.17 12.70 2.6242 4 0 0 6 38.35 1.75 2.3472 4 2 0 24 40.30 2.11 2.2380 3 3 2 12 42.17 40.01 2.1427 4 2 2 12 43.98 11.03 2.0586 5 1 0 24 43.98 16.40 2.0586 4 3 1 24 47.44 4.50 1.9165 5 2 1 24 49.10 1.31 1.8556 4 4 0 12 50.71 15.09 1.8002 5 3 0 24 53.84 18.80 1.7028 5 3 2 24 53.84 13.39 1.7028 6 1 1 12 55.35 10.41 1.6597 6 2 0 24 56.84 19.30 1.6197 5 4 1 24 59.75 12.24 1.5477 6 3 1 24 61.17 4.50 1.5151 4 4 4 4 62.57 10.72 1.4845 5 4 3 24 62.57 5.35 1.4845 7 1 0 24 63.96 1.29 1.4557 6 4 0 24 65.32 5.09 1.4285 5 5 2 12 66.68 5.36 1.4027 6 4 2 24 70.66 2.17 1.3331 7 3 2 24 70.66 1.03 1.3331 6 5 1 24 73.26 7.13 1.2921 7 4 1 24 75.83 2.40 1.2546 6 5 3 24 77.10 4.67 1.2371 6 6 0 12 77.10 6.48 1.2371 8 2 2 12 78.36 2.82 1.2203 8 3 1 24 78.36 5.93 1.2203 7 4 3 24 80.88 5.77 1.1886 7 5 2 24 83.37 2.18 1.1592 9 1 0 24 85.85 1.08 1.1319 7 6 1 24 85.85 2.08 1.1319 6 5 5 12 85.85 4.69 1.1319 9 2 1 24 87.09 1.93 1.1190 6 6 4 12 88.33 3.75 1.1065 8 5 1 24 88.33 1.09 1.1065 7 5 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.