Bi O4 P Masse R, Durif A Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences 300 (1985) 849-851 Etude structurale de la forme haute temperature du monophosphate de bismuth Bi P O4 _cod_database_code 1007149 _database_code_amcsd 0012298 CELL PARAMETERS: 4.8710 7.0730 4.7090 90.000 96.240 90.000 SPACE GROUP: P2_1/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 161.276 Density (g/cm3): 6.258 MAX. ABS. INTENSITY / VOLUME**2: 99.79427315 RIR: 5.192 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.32 26.29 4.8421 1 0 0 2 18.96 28.73 4.6811 0 0 1 2 22.25 65.50 3.9955 1 1 0 4 22.78 62.34 3.9036 0 1 1 4 24.98 100.00 3.5647 -1 0 1 2 25.18 99.04 3.5365 0 2 0 2 27.91 8.41 3.1964 1 0 1 2 28.03 3.04 3.1833 -1 1 1 4 30.69 83.04 2.9128 1 1 1 4 31.32 10.48 2.8559 1 2 0 4 31.71 8.77 2.8218 0 2 1 4 35.76 47.16 2.5106 -1 2 1 4 37.13 3.51 2.4211 2 0 0 2 37.94 2.22 2.3713 1 2 1 4 38.46 13.04 2.3406 0 0 2 2 39.33 45.66 2.2906 2 1 0 4 40.02 8.56 2.2527 -2 0 1 2 40.60 21.84 2.2220 0 1 2 4 40.96 4.86 2.2032 -1 0 2 2 42.10 5.76 2.1465 -2 1 1 4 42.65 21.29 2.1197 1 3 0 4 42.95 20.54 2.1057 0 3 1 4 43.00 21.33 2.1035 -1 1 2 4 43.93 15.70 2.0610 2 0 1 2 44.80 11.99 2.0229 1 0 2 2 45.86 1.87 1.9787 2 1 1 4 46.53 9.71 1.9518 0 2 2 4 47.88 9.31 1.9000 -2 2 1 4 47.95 28.69 1.8974 1 3 1 4 48.69 2.87 1.8700 -1 2 2 4 51.26 11.17 1.7824 -2 0 2 2 51.31 12.57 1.7807 2 2 1 4 51.70 12.14 1.7682 0 4 0 2 52.09 8.97 1.7559 1 2 2 4 52.98 2.14 1.7283 -2 1 2 4 54.31 19.56 1.6891 2 3 0 4 55.31 12.23 1.6610 0 3 2 4 55.31 2.19 1.6610 1 4 0 4 55.56 1.83 1.6542 0 4 1 4 56.50 5.07 1.6287 -2 3 1 4 57.06 3.70 1.6140 3 0 0 2 57.23 11.35 1.6097 -1 3 2 4 57.68 2.80 1.5982 2 0 2 2 57.94 10.24 1.5916 -2 2 2 4 58.24 11.00 1.5841 -1 4 1 4 59.22 4.74 1.5604 0 0 3 2 59.28 5.12 1.5589 2 1 2 4 60.00 13.93 1.5417 -3 1 1 4 60.31 3.25 1.5347 -1 0 3 2 61.87 4.80 1.4998 -1 1 3 4 62.92 3.20 1.4772 3 0 1 2 63.34 3.48 1.4683 3 2 0 4 63.92 4.17 1.4564 2 2 2 4 64.44 2.66 1.4460 3 1 1 4 64.73 1.90 1.4402 1 0 3 2 65.37 4.23 1.4276 0 2 3 4 66.22 6.64 1.4112 1 1 3 4 66.24 2.99 1.4109 0 4 2 4 66.41 3.83 1.4078 -1 2 3 4 66.72 1.41 1.4019 -3 0 2 2 67.32 2.76 1.3909 -2 4 1 4 68.20 1.97 1.3751 -3 1 2 4 68.88 5.31 1.3631 3 2 1 4 69.19 2.23 1.3578 1 5 0 4 69.29 2.98 1.3561 -2 1 3 4 69.40 2.34 1.3541 0 5 1 4 70.12 4.25 1.3420 2 4 1 4 70.62 2.60 1.3338 1 2 3 4 70.77 3.26 1.3313 1 4 2 4 71.29 4.28 1.3229 2 3 2 4 71.95 8.02 1.3124 -3 3 1 4 72.54 2.28 1.3032 -3 2 2 4 73.16 5.16 1.2936 1 5 1 4 73.65 3.90 1.2862 -1 3 3 4 75.78 4.26 1.2553 -2 4 2 4 76.03 2.47 1.2518 3 3 1 4 76.43 2.91 1.2462 3 1 2 4 77.48 2.36 1.2320 2 1 3 4 77.70 5.26 1.2290 1 3 3 4 78.27 4.66 1.2214 2 5 0 4 79.10 2.54 1.2107 0 5 2 4 79.11 2.05 1.2105 4 0 0 2 79.55 1.95 1.2049 -3 3 2 4 79.62 1.25 1.2041 -4 0 1 2 80.59 1.61 1.1921 3 4 0 4 80.59 2.36 1.1921 -2 3 3 4 80.73 2.30 1.1904 -1 5 2 4 80.90 1.64 1.1882 -3 0 3 2 81.11 1.90 1.1857 2 4 2 4 81.68 3.19 1.1788 0 6 0 2 82.28 1.72 1.1718 -3 1 3 4 82.44 2.02 1.1700 0 4 3 4 82.70 1.49 1.1669 -1 0 4 2 83.39 1.86 1.1590 -1 4 3 4 83.78 2.76 1.1546 0 1 4 4 84.62 3.91 1.1453 4 2 0 4 85.11 1.59 1.1399 -4 2 1 4 85.69 2.61 1.1337 3 4 1 4 86.26 2.17 1.1277 4 1 1 4 86.38 1.99 1.1264 -3 2 3 4 87.07 3.94 1.1192 -1 6 1 4 87.32 1.31 1.1167 1 4 3 4 87.45 2.02 1.1154 3 3 2 4 87.75 2.67 1.1123 -4 1 2 4 88.17 1.66 1.1081 -1 2 4 4 88.47 1.83 1.1051 2 3 3 4 88.82 1.26 1.1016 -2 0 4 2 89.14 1.15 1.0985 -3 4 2 4 89.31 1.42 1.0969 1 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.