Cs2 H2 O7 P2 Averbuch-Pouchot M, Durif A Comptes Rendus Hebdomadaires des Seances de l'Academie des Sciences 316 (1993) 41-46 Synthese et structure cristalline du dihydrogenodiphosphate de caesium _cod_database_code 1007211 _database_code_amcsd 0012309 CELL PARAMETERS: 7.9770 9.0640 11.4060 90.000 90.290 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 824.684 Density (g/cm3): 3.558 MAX. ABS. INTENSITY / VOLUME**2: 43.44248850 RIR: 3.976 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.54 21.09 5.7029 0 0 2 2 16.75 2.03 5.2936 1 1 1 4 19.59 19.52 4.5320 0 2 0 2 21.48 6.67 4.1376 -1 1 2 4 21.56 13.78 4.1219 1 1 2 4 22.29 13.68 3.9884 2 0 0 2 25.10 100.00 3.5481 0 2 2 4 27.22 48.97 3.2762 -2 0 2 2 27.35 37.33 3.2607 2 0 2 2 27.75 7.38 3.2152 -1 1 3 4 27.84 9.56 3.2042 1 1 3 4 29.84 63.07 2.9941 2 2 0 4 31.37 23.99 2.8515 0 0 4 2 31.67 11.20 2.8255 1 3 0 4 32.67 1.77 2.7414 1 3 1 4 33.76 18.20 2.6551 -2 2 2 4 33.87 26.77 2.6468 2 2 2 4 35.17 3.56 2.5514 3 1 0 4 35.43 9.12 2.5336 -1 3 2 4 36.03 1.10 2.4925 -3 1 1 4 36.11 4.99 2.4873 3 1 1 4 37.26 11.08 2.4135 0 2 4 4 38.34 1.65 2.3479 2 2 3 4 38.73 7.45 2.3252 -2 0 4 2 38.92 7.03 2.3141 2 0 4 2 39.71 3.70 2.2697 -1 3 3 4 39.78 9.28 2.2660 0 4 0 2 39.78 1.41 2.2658 1 3 3 4 42.35 4.75 2.1344 -1 1 5 4 42.46 6.76 2.1290 1 1 5 4 42.78 1.67 2.1139 3 1 3 4 42.95 7.77 2.1059 0 4 2 4 43.76 12.48 2.0688 -2 2 4 4 43.93 6.73 2.0610 2 2 4 4 45.13 1.15 2.0088 -1 3 4 4 45.22 4.92 2.0052 1 3 4 4 45.48 8.56 1.9942 4 0 0 2 46.07 5.98 1.9702 2 4 0 4 47.72 1.27 1.9060 -3 1 4 4 47.85 1.23 1.9010 0 0 6 2 48.25 1.57 1.8862 -3 3 2 4 48.27 3.32 1.8854 -4 0 2 2 48.37 4.54 1.8818 3 3 2 4 48.43 4.39 1.8795 4 0 2 2 48.87 7.58 1.8637 -2 4 2 4 48.95 5.25 1.8608 2 4 2 4 49.97 5.86 1.8253 4 2 0 4 50.30 1.18 1.8139 -1 1 6 4 51.44 1.31 1.7765 -1 3 5 4 51.51 5.27 1.7740 0 4 4 4 51.54 2.81 1.7733 1 3 5 4 51.71 2.34 1.7677 1 5 0 4 51.81 3.09 1.7645 3 3 3 4 52.18 7.23 1.7530 0 2 6 4 52.57 8.95 1.7408 -4 2 2 4 52.72 4.09 1.7361 4 2 2 4 53.28 2.59 1.7194 -2 0 6 2 53.50 1.64 1.7127 2 0 6 2 53.77 1.87 1.7047 -3 1 5 4 54.05 3.16 1.6965 3 1 5 4 54.31 2.18 1.6890 -1 5 2 4 54.35 5.41 1.6879 1 5 2 4 56.15 2.54 1.6381 -4 0 4 2 56.44 1.41 1.6303 4 0 4 2 56.72 2.42 1.6228 -2 4 4 4 56.87 2.68 1.6190 2 4 4 4 57.31 1.26 1.6076 -2 2 6 4 57.53 1.76 1.6021 2 2 6 4 58.66 2.50 1.5738 -1 1 7 4 58.79 2.64 1.5707 1 1 7 4 60.05 2.98 1.5406 -4 2 4 4 60.33 3.76 1.5341 4 2 4 4 61.71 1.66 1.5032 -1 5 4 4 61.95 4.07 1.4978 3 5 0 4 61.99 2.76 1.4970 4 4 0 4 63.73 2.20 1.4603 0 6 2 4 64.26 1.35 1.4496 5 1 3 4 64.27 2.16 1.4493 -4 4 2 4 64.40 2.75 1.4466 4 4 2 4 66.14 2.33 1.4127 2 6 0 4 66.15 1.93 1.4126 -1 3 7 4 66.25 1.34 1.4108 5 3 0 4 66.27 1.48 1.4104 1 3 7 4 68.13 1.52 1.3763 -3 1 7 4 68.47 2.04 1.3702 3 1 7 4 68.50 2.33 1.3697 -2 4 6 4 68.70 1.37 1.3663 2 4 6 4 70.88 1.78 1.3295 6 0 0 2 71.00 1.34 1.3276 -3 5 4 4 71.00 1.31 1.3276 -4 4 4 4 71.19 1.45 1.3245 3 5 4 4 71.49 2.04 1.3197 -4 2 6 4 73.33 1.05 1.2910 5 1 5 4 73.45 1.49 1.2891 -2 2 8 4 74.19 1.79 1.2781 1 7 0 4 74.36 1.20 1.2757 6 2 0 4 75.45 1.32 1.2599 3 3 7 4 76.34 1.25 1.2474 -1 7 2 4 76.43 1.93 1.2462 -6 2 2 4 76.61 2.50 1.2437 6 2 2 4 76.82 1.57 1.2408 -1 1 9 4 76.96 1.58 1.2389 1 1 9 4 79.37 1.11 1.2073 -6 0 4 2 82.18 1.07 1.1730 -5 5 2 4 82.33 1.15 1.1712 5 5 2 4 84.49 1.06 1.1467 6 4 0 4 85.00 1.44 1.1411 -3 7 2 4 85.09 1.61 1.1401 3 7 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.