Bassanite Bezou C, Christensen A N, Cox D, Lehmann M, Nonat A Comptes Rendus de l'Academie des Sciences Paris 312 (1991) 43-48 Structures cristallines de CaSO4,0,5H2O et CaSO4,0,6H2O Note: CaSO4*0.6H2O Locality: synthetic _database_code_amcsd 0019824 CELL PARAMETERS: 11.9991 6.9254 6.3766 90.000 90.000 90.000 SPACE GROUP: C2 X-RAY WAVELENGTH: 1.541838 Cell Volume: 529.886 Density (g/cm3): 2.763 MAX. ABS. INTENSITY / VOLUME**2: 14.02053623 RIR: 1.652 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.89 1.02 6.3766 0 0 1 2 14.77 38.42 5.9995 2 0 0 2 14.77 46.39 5.9981 1 1 0 2 20.32 2.00 4.3695 2 0 1 2 20.33 3.27 4.3690 1 1 1 2 25.72 29.71 3.4636 3 1 0 2 25.73 22.53 3.4627 0 2 0 1 29.35 4.50 3.0436 -3 1 1 2 29.35 4.43 3.0436 3 1 1 2 29.35 5.10 3.0430 0 2 1 2 29.78 32.52 2.9998 4 0 0 2 29.79 58.35 2.9990 2 2 0 2 31.78 17.07 2.8154 2 0 2 2 31.78 4.57 2.8154 -2 0 2 2 31.79 20.41 2.8153 1 1 2 2 31.79 57.95 2.8153 -1 1 2 2 33.00 2.81 2.7144 4 0 1 2 33.01 5.78 2.7139 -2 2 1 2 38.37 2.02 2.3458 -3 1 2 2 38.37 5.12 2.3458 3 1 2 2 38.38 5.22 2.3455 0 2 2 2 39.75 2.34 2.2675 5 1 0 2 39.76 1.05 2.2673 4 2 0 2 39.76 2.21 2.2669 1 3 0 2 41.32 1.74 2.1848 4 0 2 2 41.33 2.11 2.1845 -2 2 2 2 42.30 2.41 2.1365 -5 1 1 2 42.30 5.88 2.1365 5 1 1 2 42.31 1.65 2.1363 4 2 1 2 42.31 7.97 2.1363 -4 2 1 2 42.31 6.20 2.1359 -1 3 1 2 42.53 9.27 2.1255 0 0 3 2 45.26 1.14 2.0035 -1 1 3 2 45.35 1.27 1.9998 6 0 0 2 47.66 2.86 1.9082 -6 0 1 2 47.67 3.42 1.9078 -3 3 1 2 47.67 2.18 1.9078 3 3 1 2 49.32 16.91 1.8479 -5 1 2 2 49.32 2.92 1.8479 5 1 2 2 49.32 16.76 1.8477 4 2 2 2 49.32 2.23 1.8477 -4 2 2 2 49.33 22.52 1.8475 1 3 2 2 52.87 5.12 1.7318 6 2 0 2 52.88 1.15 1.7313 0 4 0 1 54.14 8.41 1.6942 6 0 2 2 54.15 10.75 1.6939 -3 3 2 2 54.15 2.25 1.6939 3 3 2 2 55.20 3.70 1.6639 7 1 0 2 55.21 5.12 1.6637 5 3 0 2 55.22 3.76 1.6635 2 4 0 2 60.05 1.69 1.5407 -2 0 4 2 60.05 1.63 1.5407 1 1 4 2 60.87 1.64 1.5218 -6 2 2 2 60.87 1.03 1.5218 6 2 2 2 63.01 2.57 1.4751 -7 1 2 2 63.02 2.24 1.4750 5 3 2 2 63.03 1.30 1.4748 2 4 2 2 64.33 1.40 1.4481 -3 1 4 2 64.33 1.05 1.4481 3 1 4 2 64.33 2.81 1.4481 0 2 4 2 69.24 2.77 1.3569 4 4 2 2 72.17 1.91 1.3090 6 4 0 2 72.17 1.79 1.3088 3 5 0 2 72.48 4.85 1.3041 5 1 4 2 72.48 4.37 1.3041 -4 2 4 2 72.48 3.53 1.3040 -1 3 4 2 75.19 3.05 1.2636 8 2 2 2 75.20 3.32 1.2635 -7 3 2 2 75.21 2.41 1.2633 -1 5 2 2 76.40 2.55 1.2466 -6 0 4 2 76.41 4.54 1.2464 3 3 4 2 79.07 1.15 1.2111 -9 1 2 2 79.09 1.55 1.2108 3 5 2 2 82.20 1.48 1.1727 0 4 4 2 83.79 2.97 1.1545 9 3 0 2 83.81 1.52 1.1542 0 6 0 1 86.70 1.49 1.1230 10 0 2 2 86.73 2.08 1.1228 -5 5 2 2 89.79 1.57 1.0922 -4 4 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.