Gunningite Le Fur Y, Coing-Boyat J, Bassi G Comptes Rendus de l'Academie des Sciences Paris C262 (1966) 632-635 Structure des sulfates monohydrates, monocliniques, des metaux de transition, MSO4*H2O (M = Mn, Fe, Co, Ni et Zn) Locality: synthetic _database_code_amcsd 0021020 CELL PARAMETERS: 6.9300 7.5840 7.5030 90.000 116.233 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 353.721 Density (g/cm3): 3.411 MAX. ABS. INTENSITY / VOLUME**2: 30.23658518 RIR: 2.887 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.45 22.60 4.8076 1 1 0 4 18.66 5.72 4.7559 -1 1 1 4 23.46 44.52 3.7920 0 2 0 2 26.21 5.94 3.4006 1 1 1 4 26.64 100.00 3.3462 -1 1 2 4 26.99 27.15 3.3037 0 2 1 4 28.72 60.82 3.1081 2 0 0 2 29.25 1.27 3.0528 -2 0 2 2 35.09 14.10 2.5576 -2 2 1 4 35.67 5.24 2.5169 0 2 2 4 37.41 4.70 2.4038 2 2 0 4 37.50 11.03 2.3985 1 1 2 4 37.83 3.69 2.3780 -2 2 2 4 38.02 2.46 2.3665 -1 1 3 4 38.44 17.63 2.3418 1 3 0 4 41.56 7.04 2.1728 -3 1 2 4 43.24 27.23 2.0924 -1 3 2 4 44.13 9.45 2.0524 2 2 1 4 44.86 1.55 2.0204 -2 2 3 4 45.37 11.46 1.9988 3 1 0 4 47.07 2.08 1.9308 0 2 3 4 47.82 1.72 1.9023 2 0 2 2 47.98 2.94 1.8960 0 4 0 2 48.85 12.64 1.8644 -2 0 4 2 51.01 3.78 1.7904 -1 1 4 4 51.09 5.05 1.7876 1 3 2 4 52.86 2.25 1.7321 -4 0 2 2 53.92 7.07 1.7003 2 2 2 4 54.27 3.28 1.6904 -3 1 4 4 54.35 5.26 1.6881 -3 3 2 4 54.54 3.60 1.6826 0 0 4 2 54.87 14.77 1.6731 -2 2 4 4 55.64 10.85 1.6519 0 4 2 4 57.19 10.52 1.6106 -2 4 2 4 57.51 9.53 1.6025 3 3 0 4 58.59 3.64 1.5755 -4 2 2 4 59.48 7.62 1.5541 4 0 0 2 60.04 2.02 1.5409 -4 2 1 4 60.17 5.19 1.5380 0 2 4 4 60.63 1.15 1.5272 -4 2 3 4 60.67 3.06 1.5264 -4 0 4 2 62.36 1.26 1.4890 -1 3 4 4 63.09 2.06 1.4736 1 5 0 4 63.46 4.24 1.4659 3 1 2 4 64.33 1.13 1.4481 0 4 3 4 64.64 4.43 1.4418 1 1 4 4 64.84 2.62 1.4380 4 2 0 4 65.25 1.44 1.4300 -3 3 4 4 65.97 3.07 1.4160 -4 2 4 4 66.56 2.27 1.4050 -1 5 2 4 67.08 1.02 1.3953 -2 2 5 4 69.11 2.95 1.3591 -5 1 2 4 70.07 7.63 1.3429 2 4 2 4 72.63 1.15 1.3017 4 2 1 4 72.97 2.50 1.2964 -5 1 4 4 73.65 2.04 1.2862 3 3 2 4 74.15 6.71 1.2788 -4 4 2 4 74.25 1.02 1.2773 -4 2 5 4 74.76 1.94 1.2699 1 3 4 4 75.16 1.77 1.2641 2 0 4 2 77.88 3.96 1.2265 -3 1 6 4 78.08 2.43 1.2239 3 5 0 4 78.98 2.34 1.2123 -5 3 2 4 80.01 2.80 1.1992 2 2 4 4 81.11 1.74 1.1857 -1 1 6 4 81.31 2.72 1.1833 0 6 2 4 81.31 1.18 1.1832 -2 2 6 4 82.35 2.55 1.1710 -1 5 4 4 82.62 2.71 1.1679 -2 6 2 4 82.68 1.77 1.1672 -5 3 4 4 84.95 2.29 1.1417 -3 5 4 4 85.22 1.17 1.1387 -4 2 6 4 87.45 1.45 1.1154 -3 3 6 4 88.90 1.37 1.1008 -5 1 6 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.