Bixbyite-(Fe) Danno T, Nakatsuka D, Kusano Y, Asaoka H, Nakanishi M, Fujii T, Ikeda Y, Takada J Crystal Growth & Design 13 (2013) 770-774 Crystal structure of beta-Fe2O3 and topotactic phase transformation to alpha-Fe2O3 Locality: synthetic _database_code_amcsd 0021095 CELL PARAMETERS: 9.4039 9.4039 9.4039 90.000 90.000 90.000 SPACE GROUP: Ia3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 831.618 Density (g/cm3): 5.101 MAX. ABS. INTENSITY / VOLUME**2: 94.07258074 RIR: 6.005 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.17 14.29 3.8391 2 1 1 24 33.00 100.00 2.7147 2 2 2 8 38.28 17.13 2.3510 4 0 0 6 40.71 4.39 2.2165 4 1 1 24 45.23 8.90 2.0049 3 3 2 24 47.36 1.15 1.9196 4 2 2 24 49.42 5.20 1.8443 4 3 1 24 49.42 3.82 1.8443 4 1 3 24 53.36 1.94 1.7169 5 2 1 24 53.36 1.60 1.7169 5 1 2 24 55.26 41.17 1.6624 4 4 0 12 57.11 2.04 1.6128 4 3 3 24 60.71 3.29 1.5255 6 1 1 24 60.71 1.08 1.5255 5 2 3 24 64.18 2.62 1.4511 5 4 1 24 64.18 1.69 1.4511 5 1 4 24 65.88 21.67 1.4177 6 2 2 24 67.56 2.90 1.3865 6 3 1 24 67.56 2.60 1.3865 6 1 3 24 69.22 2.85 1.3573 4 4 4 8 70.86 1.11 1.3299 5 3 4 24 74.09 1.89 1.2797 7 1 2 24 75.68 1.11 1.2566 6 2 4 24 81.97 3.46 1.1755 8 0 0 6 83.52 1.40 1.1575 8 1 1 24 88.15 1.14 1.1083 8 2 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.