Pyromorphite Barinova A V, Bonin M, Pushcharovsky D Y, Rastsvetaeva R K, Schenk K, Dimitrova O V Crystallography Reports 43 (1998) 189-192 Crystal structure of synthetic hydroxylpyromorphite Pb5(PO4)3(OH) Locality: synthetic Note: y(O3) corrected _database_code_amcsd 0012355 CELL PARAMETERS: 9.7740 9.7740 7.2910 90.000 90.000 120.000 SPACE GROUP: P6_3/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 603.201 Density (g/cm3): 7.360 MAX. ABS. INTENSITY / VOLUME**2: 180.2396266 RIR: 7.974 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.15 12.26 4.8870 1 1 0 6 20.99 30.55 4.2323 2 0 0 6 21.89 31.25 4.0595 1 1 1 12 24.32 1.25 3.6603 2 0 1 12 24.42 7.40 3.6455 0 0 2 2 26.62 44.50 3.3482 1 0 2 12 27.89 25.28 3.1993 1 2 0 6 27.89 22.01 3.1993 2 1 0 6 30.51 53.30 2.9297 1 2 1 12 30.51 46.70 2.9297 2 1 1 12 30.59 80.16 2.9221 1 1 2 12 31.71 32.95 2.8215 3 0 0 6 32.41 1.26 2.7621 2 0 2 12 36.78 2.04 2.4435 2 2 0 6 37.40 1.47 2.4046 2 1 2 12 38.87 4.12 2.3168 2 2 1 12 40.36 1.31 2.2347 1 3 1 12 40.43 12.12 2.2313 3 0 2 12 41.50 11.54 2.1761 1 1 3 12 42.73 4.59 2.1161 4 0 0 6 44.64 33.43 2.0297 2 2 2 12 45.98 8.13 1.9738 1 3 2 12 45.98 5.87 1.9738 3 1 2 12 46.78 2.11 1.9419 2 3 0 6 46.78 5.43 1.9419 3 2 0 6 46.95 14.03 1.9353 1 2 3 12 46.95 15.45 1.9353 2 1 3 12 48.51 6.40 1.8765 2 3 1 12 48.51 7.87 1.8765 3 2 1 12 49.34 16.61 1.8471 1 4 0 6 49.34 11.99 1.8471 4 1 0 6 49.83 28.78 1.8301 4 0 2 12 50.04 11.84 1.8227 0 0 4 2 53.67 2.48 1.7078 1 1 4 12 54.84 3.83 1.6741 2 0 4 12 57.62 1.64 1.5996 2 4 0 6 57.62 3.65 1.5996 4 2 0 6 58.01 8.56 1.5898 3 3 1 12 58.26 4.91 1.5837 1 2 4 12 58.26 7.26 1.5837 2 1 4 12 60.28 12.02 1.5354 5 0 2 12 60.47 7.41 1.5311 3 0 4 12 61.08 1.85 1.5171 3 2 3 12 61.08 3.71 1.5171 2 3 3 12 62.40 2.46 1.4883 1 5 1 12 62.40 1.23 1.4883 5 1 1 12 62.44 11.93 1.4873 3 3 2 12 66.97 1.29 1.3973 1 1 5 12 67.86 2.09 1.3811 4 0 4 12 69.46 3.88 1.3532 3 3 3 12 70.69 2.76 1.3326 2 5 1 12 70.69 1.42 1.3326 5 2 1 12 70.91 2.18 1.3290 3 2 4 12 71.04 2.96 1.3269 2 1 5 12 71.04 4.05 1.3269 1 2 5 12 71.74 4.54 1.3157 6 0 2 12 72.74 1.13 1.3001 4 3 2 12 72.91 8.57 1.2974 1 4 4 12 72.91 7.25 1.2974 4 1 4 12 73.34 1.81 1.2908 1 6 0 6 73.34 1.89 1.2908 6 1 0 6 73.47 1.11 1.2889 1 5 3 12 74.68 1.94 1.2711 1 6 1 12 74.68 2.84 1.2711 6 1 1 12 74.72 5.99 1.2704 5 2 2 12 74.72 5.33 1.2704 2 5 2 12 78.25 1.45 1.2218 4 4 0 6 79.72 1.80 1.2028 1 0 6 12 79.76 1.99 1.2023 2 4 4 12 79.76 2.36 1.2023 4 2 4 12 81.27 1.94 1.1838 2 5 3 12 81.65 4.39 1.1793 1 1 6 12 82.77 1.50 1.1660 3 2 5 12 85.10 1.66 1.1400 6 1 3 12 85.10 1.07 1.1400 1 6 3 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.