Sr3La(PO4)3 Barbier J, Greedan J E, Asaro T, McCarthy G J European Journal of Solid State and Inorganic Chemistry 27 (1990) 855-867 Neutron diffraction study of disorder in eulytite-type Sr3La(PO4)3 Locality: synthetic Sample: T = 298 K _database_code_amcsd 0012536 CELL PARAMETERS: 10.1853 10.1853 10.1853 90.000 90.000 90.000 SPACE GROUP: I-43d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1056.626 Density (g/cm3): 4.316 MAX. ABS. INTENSITY / VOLUME**2: 83.75881123 RIR: 6.319 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.37 6.55 4.1581 2 1 1 12 24.72 21.32 3.6010 2 2 0 12 27.70 100.00 3.2209 3 1 0 24 32.90 36.79 2.7221 3 2 1 24 41.59 17.28 2.1715 3 3 2 12 43.53 17.41 2.0791 4 2 2 12 45.40 12.97 1.9975 5 1 0 24 45.40 30.52 1.9975 4 3 1 24 48.98 9.37 1.8596 5 2 1 24 55.63 9.03 1.6523 5 3 2 24 55.63 2.97 1.6523 6 1 1 12 57.20 5.86 1.6104 6 2 0 24 58.75 8.38 1.5716 5 4 1 24 61.77 2.64 1.5017 6 3 1 24 63.25 4.62 1.4701 4 4 4 4 67.59 2.13 1.3860 6 3 3 12 67.59 5.75 1.3860 7 2 1 24 67.59 1.00 1.3860 5 5 2 12 69.00 6.10 1.3611 6 4 2 24 70.40 1.33 1.3374 7 3 0 24 73.16 4.25 1.2935 6 5 1 24 73.16 1.09 1.2935 7 3 2 24 74.53 1.33 1.2732 8 0 0 6 78.58 1.86 1.2174 6 5 3 24 79.92 2.69 1.2003 8 2 2 12 81.25 2.94 1.1840 7 4 3 24 81.25 2.31 1.1840 7 5 0 24 81.25 2.14 1.1840 8 3 1 24 83.90 2.07 1.1533 7 5 2 24 89.16 1.44 1.0983 9 2 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.