Na3La2(CO3)4F Mercier N, Taulelle F, Leblanc M European Journal of Solid State and Inorganic Chemistry 30 (1993) 609-617 Growth, structure, NMR characterization of a new fluorocarbonate Na3La2(CO3)4F _cod_database_code 1000343 _database_code_amcsd 0012579 CELL PARAMETERS: 5.0830 5.0830 23.0340 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 515.395 Density (g/cm3): 3.903 MAX. ABS. INTENSITY / VOLUME**2: 32.66993508 RIR: 2.725 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.68 17.80 11.5170 0 0 2 2 15.39 51.59 5.7585 0 0 4 2 20.17 21.98 4.4020 1 0 0 6 20.54 100.00 4.3238 1 0 1 12 21.61 8.65 4.1119 1 0 2 12 23.17 24.76 3.8390 0 0 6 2 23.29 24.61 3.8189 1 0 3 12 25.47 35.51 3.4972 1 0 4 12 28.04 70.96 3.1826 1 0 5 12 30.91 49.71 2.8933 1 0 6 12 34.02 7.26 2.6356 1 0 7 12 35.32 68.90 2.5415 1 1 0 6 36.19 5.03 2.4818 1 1 2 12 37.32 11.91 2.4096 1 0 8 12 38.73 19.98 2.3251 1 1 4 12 39.11 19.30 2.3034 0 0 10 2 40.78 35.81 2.2126 1 0 9 12 41.01 17.73 2.2010 2 0 0 6 41.20 36.51 2.1910 2 0 1 12 42.67 20.54 2.1192 1 1 6 12 44.05 9.64 2.0559 2 0 4 12 44.39 3.33 2.0409 1 0 10 12 45.68 61.12 1.9860 2 0 5 12 47.62 11.90 1.9094 2 0 6 12 47.73 21.46 1.9054 1 1 8 12 48.12 15.91 1.8910 1 0 11 12 53.70 25.94 1.7067 1 1 10 12 55.03 10.93 1.6688 2 0 9 12 55.21 3.78 1.6638 2 1 0 12 55.36 20.00 1.6595 2 1 1 24 55.88 1.55 1.6453 0 0 14 2 55.94 14.88 1.6437 1 0 13 12 56.60 4.72 1.6261 2 1 3 24 57.67 5.76 1.5984 2 1 4 24 57.95 3.71 1.5913 2 0 10 12 59.03 19.35 1.5649 2 1 5 24 60.03 2.37 1.5412 1 0 14 12 60.66 4.33 1.5266 2 1 6 24 61.08 5.27 1.5171 2 0 11 12 63.39 10.81 1.4673 3 0 0 6 64.24 7.08 1.4499 1 0 15 12 64.71 2.73 1.4406 2 1 8 24 65.66 4.50 1.4219 3 0 4 12 67.10 12.64 1.3949 2 1 9 24 67.86 7.11 1.3811 1 1 14 12 67.91 1.01 1.3802 2 0 13 12 68.45 4.10 1.3706 3 0 6 12 68.58 2.23 1.3683 1 0 16 12 69.72 3.58 1.3487 2 1 10 24 71.61 1.49 1.3178 2 0 14 12 72.27 4.84 1.3074 3 0 8 12 72.57 9.57 1.3027 2 1 11 24 74.70 11.84 1.2708 2 2 0 6 75.49 2.91 1.2594 2 0 15 12 75.97 1.57 1.2526 1 1 16 12 76.82 3.85 1.2409 2 2 4 12 77.06 8.55 1.2376 3 0 10 12 77.71 1.57 1.2288 1 0 18 12 78.31 1.47 1.2209 3 1 0 12 78.44 5.80 1.2192 3 1 1 24 78.93 8.49 1.2129 2 1 13 24 79.44 4.27 1.2064 2 2 6 12 79.49 1.16 1.2057 3 1 3 24 80.40 2.62 1.1943 3 1 4 24 81.57 8.56 1.1802 3 1 5 24 82.44 4.20 1.1699 2 1 14 24 82.54 6.73 1.1688 1 0 19 12 83.00 3.87 1.1635 3 1 6 24 84.83 5.66 1.1430 1 1 18 12 86.18 5.24 1.1284 2 1 15 24 86.61 1.11 1.1240 3 1 8 24 87.71 7.13 1.1127 2 2 10 12 88.79 6.60 1.1019 3 1 9 24 89.07 3.10 1.0992 4 0 1 12 89.49 3.97 1.0951 3 0 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.