Ce0.5 Cu2 Nd1.5 O9 Pb0.5 Sr2.5 Gambardella M, Domenges B, Rouillon T, Hervieu M, Raveau B European Journal of Solid State and Inorganic Chemistry 39 (1992) 333-345 Introduction of fluorite layers in the 1212-type structure: the oxide (Pb.5Sr.5)Sr2Nd2-xCexCu2O9-d _cod_database_code 1001531 _database_code_amcsd 0012629 CELL PARAMETERS: 3.8783 3.8783 29.4950 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 443.641 Density (g/cm3): 6.588 MAX. ABS. INTENSITY / VOLUME**2: 183.7737591 RIR: 9.083 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 5.99 13.76 14.7475 0 0 2 2 12.00 1.06 7.3738 0 0 4 2 18.05 2.68 4.9158 0 0 6 2 24.68 22.74 3.6077 1 0 3 8 30.30 5.41 2.9495 0 0 10 2 31.35 100.00 2.8535 1 0 7 8 32.65 53.03 2.7424 1 1 0 4 34.91 1.38 2.5704 1 1 4 8 35.87 4.67 2.5032 1 0 9 8 40.92 1.14 2.2056 1 0 11 8 42.93 8.89 2.1068 0 0 14 2 45.14 18.86 2.0084 1 1 10 8 46.36 5.65 1.9584 1 0 13 8 46.85 28.48 1.9391 2 0 0 4 53.66 4.49 1.7081 2 1 3 16 54.96 13.17 1.6707 1 1 14 8 56.82 3.34 1.6203 2 0 10 8 57.46 30.10 1.6039 2 1 7 16 58.26 6.96 1.5837 1 0 17 8 60.38 1.49 1.5330 2 1 9 16 63.03 1.82 1.4748 0 0 20 2 65.41 8.00 1.4268 2 0 14 8 68.04 2.96 1.3779 2 1 13 16 68.42 7.13 1.3712 2 2 0 4 71.43 1.45 1.3206 1 0 21 8 72.82 2.15 1.2989 1 1 20 8 76.63 1.21 1.2434 2 2 10 8 77.18 5.32 1.2359 3 0 7 8 77.88 4.93 1.2266 2 1 17 16 77.89 6.08 1.2264 3 1 0 8 82.10 2.81 1.1738 2 0 20 8 84.26 3.29 1.1492 2 2 14 8 85.81 3.68 1.1324 3 1 10 16 86.85 1.75 1.1215 1 1 24 8 89.87 1.42 1.0915 2 1 21 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.