Cs O4 P Zn Blum D, Durif A, Averbuch-Pouchot M Ferroelectrics 69 (1986) 283-292 Crystal structures of the three forms of Cs Zn P O4 _cod_database_code 1007237 _database_code_amcsd 0015919 CELL PARAMETERS: 9.2360 5.4620 9.3420 90.000 90.000 90.000 SPACE GROUP: Pn2_1a X-RAY WAVELENGTH: 1.541838 Cell Volume: 471.276 Density (g/cm3): 4.133 MAX. ABS. INTENSITY / VOLUME**2: 63.42997000 RIR: 4.997 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.48 2.02 6.5680 1 0 1 4 18.82 8.98 4.7152 0 1 1 2 19.00 2.44 4.6710 0 0 2 2 19.22 1.55 4.6180 2 0 0 2 21.16 1.63 4.1996 1 1 1 4 25.25 3.10 3.5265 2 1 0 2 26.91 70.14 3.3136 1 1 2 4 27.03 100.00 3.2993 2 1 1 4 27.15 39.84 3.2840 2 0 2 4 30.29 14.64 2.9508 1 0 3 4 30.57 19.47 2.9240 3 0 1 4 32.79 31.21 2.7310 0 2 0 1 33.11 35.22 2.7052 0 1 3 2 34.75 1.14 2.5819 2 0 3 4 38.17 4.94 2.3576 0 2 2 2 38.29 7.72 2.3507 2 2 0 2 38.57 3.10 2.3342 2 1 3 4 39.01 9.09 2.3090 4 0 0 2 39.45 1.22 2.2844 1 2 2 4 41.23 6.05 2.1893 3 0 3 4 42.51 1.00 2.1268 4 1 0 2 43.08 9.80 2.0998 2 2 2 4 43.26 6.00 2.0916 1 1 4 4 43.65 13.37 2.0737 4 1 1 4 43.73 4.79 2.0699 4 0 2 4 45.24 8.74 2.0043 1 2 3 4 45.44 11.44 1.9958 3 2 1 4 49.79 10.78 1.8313 1 0 5 4 51.11 1.08 1.7870 0 3 1 2 51.85 2.79 1.7632 4 2 0 2 51.91 22.79 1.7613 3 1 4 4 52.07 1.34 1.7563 4 1 3 4 53.26 2.12 1.7199 5 1 1 4 53.65 5.67 1.7082 3 2 3 4 55.04 7.74 1.6684 1 3 2 4 55.11 10.71 1.6666 2 3 1 4 55.46 2.10 1.6568 2 2 4 4 55.72 8.62 1.6496 4 2 2 4 56.00 1.02 1.6420 4 0 4 4 56.13 9.30 1.6386 5 1 2 4 58.06 2.16 1.5887 5 0 3 4 58.75 6.91 1.5717 0 3 3 2 60.11 2.79 1.5393 6 0 0 2 60.91 10.82 1.5210 1 2 5 4 62.88 3.49 1.4781 1 1 6 4 63.00 1.52 1.4754 2 0 6 4 63.58 2.05 1.4633 6 1 1 4 65.82 1.56 1.4189 1 3 4 4 66.12 3.96 1.4132 4 3 1 4 68.30 2.22 1.3733 5 2 3 4 68.74 3.37 1.3655 0 4 0 1 69.85 3.14 1.3465 3 1 6 4 70.18 5.41 1.3410 6 2 0 2 70.37 6.07 1.3379 6 1 3 4 71.87 3.78 1.3136 5 0 5 4 72.66 7.42 1.3013 3 3 4 4 72.87 2.07 1.2981 2 2 6 4 72.97 2.39 1.2964 0 1 7 2 75.39 3.29 1.2608 2 4 2 4 76.20 3.42 1.2494 5 3 2 4 76.94 1.53 1.2392 1 4 3 4 77.09 2.08 1.2372 3 4 1 4 78.04 2.19 1.2245 3 0 7 4 81.27 5.27 1.1838 5 2 5 4 82.12 1.54 1.1737 1 3 6 4 83.02 1.36 1.1632 5 1 6 4 83.42 1.36 1.1586 3 4 3 4 85.12 1.19 1.1398 4 4 2 4 85.72 1.53 1.1333 1 1 8 4 86.59 1.59 1.1242 7 1 4 4 86.86 2.59 1.1214 8 1 1 4 87.26 3.29 1.1173 3 2 7 4 87.98 1.21 1.1100 7 2 3 4 88.53 1.47 1.1045 3 3 6 4 89.01 2.44 1.0998 6 3 3 4 89.54 3.11 1.0947 1 4 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.