Titanium
      Chebotareva E S, Nuzhdina S G
      Fizika Metallov i Metallovedenie 36 (1973) 200-202
      Observation of omega-titanium in a composite hard facing alloy based
      on fine-grain diamonds
      Locality: synthetic
      Sample: at P = 4 GPa, known as the omega phase
      _database_code_amcsd 0012644

      CELL PARAMETERS:    4.6000   4.6000   2.8200   90.000   90.000  120.000
      SPACE GROUP: P6/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     51.677
      Density (g/cm3):      4.614
      MAX. ABS. INTENSITY / VOLUME**2:      68.33029405    
      RIR:      4.822
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                31.73          7.01        2.8200    0   0   1         2
                39.14         89.10        2.3017    1   0   1        12
                39.17        100.00        2.3000    1   1   0         6
                51.26          9.00        1.7824    1   1   1        12
                56.57         25.22        1.6269    2   0   1        12
                66.29          5.25        1.4100    0   0   2         2
                70.96         21.80        1.3282    2   1   1        24
                70.98         12.25        1.3279    3   0   0         6
                79.78         16.29        1.2021    1   1   2        12
                79.84          1.81        1.2014    3   0   1        12
                84.19          2.29        1.1500    2   2   0         6
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.