Lueshite Mishchuk D O, V'yunov O I, Ovchar O V, Belous A G Inorganic Materials 40 (2004) 1324-1330 Structural and dielectric properties of solid solutions of sodium niobate in lanthanum and neodymium niobates Locality: synthetic Note: Nb2/3-x Na3x Nb2O6 synthesized at 1330 deg C Note: x = .58, Nd.09Na1.74Nb2O6 _database_code_amcsd 0018682 CELL PARAMETERS: 5.5100 5.5563 15.5670 90.000 90.000 90.000 SPACE GROUP: Pbcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 476.587 Density (g/cm3): 4.665 MAX. ABS. INTENSITY / VOLUME**2: 64.60186300 RIR: 4.509 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.73 81.02 3.9124 1 1 0 4 22.85 38.25 3.8918 0 0 4 2 32.22 26.99 2.7782 0 2 0 2 32.45 100.00 2.7592 1 1 4 8 32.50 24.22 2.7550 2 0 0 2 38.35 1.85 2.3473 1 0 6 4 39.87 1.82 2.2611 0 2 4 4 40.10 2.31 2.2486 2 0 4 4 46.42 37.01 1.9562 2 2 0 4 46.68 17.72 1.9459 0 0 8 2 52.10 7.56 1.7556 1 3 0 4 52.34 12.87 1.7478 2 2 4 8 52.47 6.68 1.7439 3 1 0 4 52.52 13.69 1.7423 1 1 8 8 55.24 1.02 1.6630 1 3 3 8 57.60 17.03 1.6003 1 3 4 8 57.85 10.29 1.5938 0 2 8 4 57.95 19.41 1.5914 3 1 4 8 58.03 9.86 1.5894 2 0 8 4 67.42 4.14 1.3891 0 4 0 2 67.95 16.11 1.3796 2 2 8 8 68.06 3.95 1.3775 4 0 0 2 72.21 1.68 1.3082 0 4 4 4 72.47 1.57 1.3041 3 3 0 4 72.52 4.58 1.3035 1 3 8 8 72.83 4.15 1.2987 3 1 8 8 72.84 2.43 1.2986 4 0 4 4 76.86 3.24 1.2403 2 4 0 4 77.14 5.66 1.2366 3 3 4 8 77.32 2.88 1.2341 4 2 0 4 77.52 6.20 1.2313 1 1 12 8 81.44 1.25 1.1818 2 4 4 8 81.89 1.59 1.1764 4 2 4 8 85.98 3.44 1.1306 0 4 8 4 86.58 3.15 1.1243 4 0 8 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.