Bixbyite-(Mn) Morozov I S, Kuznetsov V G Izvestiya Akademii Nauk SSSR 1949 (1949) 343-353 The crystal structure of Mn2O3 Locality: synthetic _database_code_amcsd 0021096 CELL PARAMETERS: 9.4080 9.4080 9.4080 90.000 90.000 90.000 SPACE GROUP: Ia3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 832.706 Density (g/cm3): 5.036 MAX. ABS. INTENSITY / VOLUME**2: 85.41356349 RIR: 5.522 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.16 16.63 3.8408 2 1 1 24 32.98 100.00 2.7159 2 2 2 8 38.27 14.78 2.3520 4 0 0 6 40.69 3.61 2.2175 4 1 1 24 45.21 6.48 2.0058 3 3 2 24 49.40 3.20 1.8451 4 3 1 24 49.40 3.71 1.8451 4 1 3 24 55.23 45.78 1.6631 4 4 0 12 57.08 1.41 1.6135 4 3 3 24 60.68 1.93 1.5262 6 1 1 24 64.15 1.33 1.4517 5 4 1 24 64.15 1.61 1.4517 5 1 4 24 65.85 22.46 1.4183 6 2 2 24 67.53 2.37 1.3871 6 3 1 24 67.53 2.64 1.3871 6 1 3 24 69.18 2.40 1.3579 4 4 4 8 74.05 1.17 1.2803 7 2 1 24 81.92 4.06 1.1760 8 0 0 6 83.47 1.21 1.1580 8 1 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.