Boracite Mehmel M Fortschritte der Mineralogie 17 (1932) 436-438 Kristallstrukturelle Untersuchungen an Borazit Locality: synthetic Note: this is the high-temperature modification _cod_database_code 1011284 _database_code_amcsd 0018134 CELL PARAMETERS: 12.1000 12.1000 12.1000 90.000 90.000 90.000 SPACE GROUP: F-43c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1771.561 Density (g/cm3): 2.939 MAX. ABS. INTENSITY / VOLUME**2: 9.114683692 RIR: 1.010 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.76 21.05 4.2780 2 2 0 12 25.50 100.00 3.4930 2 2 2 4 29.53 73.59 3.0250 4 0 0 6 33.11 4.71 2.7056 4 2 0 24 36.37 28.87 2.4699 4 2 2 12 42.25 84.09 2.1390 4 4 0 12 44.29 17.61 2.0453 5 3 1 24 44.95 22.07 2.0167 4 4 2 12 44.95 26.48 2.0167 6 0 0 6 47.53 2.74 1.9132 6 2 0 24 50.00 32.29 1.8241 6 2 2 12 52.39 30.07 1.7465 4 4 4 4 54.70 5.60 1.6780 6 4 0 24 56.95 3.39 1.6169 6 4 2 24 58.60 6.79 1.5753 7 3 1 24 61.29 2.33 1.5125 8 0 0 6 63.39 3.18 1.4673 6 4 4 12 63.39 2.71 1.4673 8 2 0 24 65.45 5.34 1.4260 8 2 2 12 65.45 1.40 1.4260 6 6 0 12 66.98 1.44 1.3972 7 5 1 24 67.48 4.36 1.3880 6 6 2 12 69.48 16.94 1.3528 8 4 0 24 70.96 2.59 1.3281 7 5 3 24 71.46 9.15 1.3202 8 4 2 24 73.41 1.88 1.2899 6 6 4 12 77.25 27.22 1.2350 8 4 4 12 81.04 1.40 1.1865 10 2 0 24 82.45 2.16 1.1698 9 5 1 24 82.92 1.46 1.1643 10 2 2 12 86.19 1.01 1.1283 9 5 3 24 86.66 1.62 1.1235 10 4 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.