Ca0.75 Cd0.25 O Natta G, Passerini L Gazzetta Chimica Italiana 59 (1929) 129-143 Soluzioni solide, isomorfismo e simmorfismo tra gli ossidi dei metalli bivalenti. - 1. Sistemi: CaO-CdO, CaO-MnO, CaO-CoO, CaO-NiO, CaO-MgO. _cod_database_code 1010883 _database_code_amcsd 0017613 CELL PARAMETERS: 4.7750 4.7750 4.7750 90.000 90.000 90.000 SPACE GROUP: Fm3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 108.873 Density (g/cm3): 4.524 MAX. ABS. INTENSITY / VOLUME**2: 79.22303020 RIR: 5.702 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.48 66.15 2.7568 1 1 1 8 37.68 100.00 2.3875 2 0 0 6 54.34 55.28 1.6882 2 2 0 12 64.75 22.19 1.4397 3 1 1 24 68.01 15.49 1.3784 2 2 2 8 80.45 6.26 1.1938 4 0 0 6 89.46 7.93 1.0955 3 3 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.