Cu Fe N6 Rb2 Rigamonti R Gazzetta Chimica Italiana 67 (1937) 146-158 Struttura dei cupriferrocianuri.- Nota II. Ferrocianuri di rame e cationi monovalenti _cod_database_code 1010364 _database_code_amcsd 0017290 CELL PARAMETERS: 9.9800 9.9800 9.9800 90.000 90.000 90.000 SPACE GROUP: F-43m X-RAY WAVELENGTH: 1.541838 Cell Volume: 994.012 Density (g/cm3): 2.983 MAX. ABS. INTENSITY / VOLUME**2: 76.18645289 RIR: 8.317 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.77 1.55 4.9900 2 0 0 6 25.24 100.00 3.5285 2 2 0 12 31.04 11.84 2.8810 2 2 2 4 36.00 39.65 2.4950 4 0 0 6 44.47 28.39 2.0372 4 2 2 12 51.82 18.37 1.7642 4 4 0 12 58.49 22.43 1.5780 6 2 0 24 64.71 4.29 1.4405 4 4 4 4 70.63 17.69 1.3336 6 4 2 24 76.34 2.18 1.2475 8 0 0 6 81.91 2.43 1.1762 8 2 2 12 81.91 4.56 1.1762 6 6 0 12 87.40 4.51 1.1158 8 4 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.