Lithiophosphate Keffer C, Mighell A D, Mauer F, Swanson H, Block S Inorganic Chemistry 6 (1967) 119-125 The crystal structure of twinned low-temperature lithium phosphate Locality: synthetic _database_code_amcsd 0012673 CELL PARAMETERS: 6.1150 5.2394 4.8554 90.000 90.000 90.000 SPACE GROUP: Pmn2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 155.562 Density (g/cm3): 2.472 MAX. ABS. INTENSITY / VOLUME**2: 7.519090868 RIR: 0.991 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.92 26.93 5.2394 0 1 0 2 22.34 94.42 3.9787 1 1 0 4 23.39 100.00 3.8025 1 0 1 2 25.00 56.98 3.5613 0 1 1 2 29.01 18.31 3.0774 1 1 1 4 29.21 15.78 3.0575 2 0 0 2 33.95 59.15 2.6407 2 1 0 4 34.23 32.51 2.6197 0 2 0 2 37.03 50.82 2.4277 0 0 2 1 37.34 1.79 2.4080 1 2 0 4 38.82 33.59 2.3198 2 1 1 4 39.07 15.58 2.3055 0 2 1 2 40.97 1.10 2.2027 0 1 2 2 41.88 5.70 2.1573 1 2 1 4 43.68 4.45 2.0724 1 1 2 4 47.84 1.43 1.9013 2 0 2 2 48.43 3.86 1.8794 3 0 1 2 49.52 5.75 1.8408 2 2 1 4 51.11 14.96 1.7872 2 1 2 4 51.31 6.93 1.7807 0 2 2 2 51.67 7.45 1.7691 3 1 1 4 53.61 1.80 1.7096 1 2 2 4 54.65 3.28 1.6793 1 3 0 4 55.95 2.37 1.6434 0 3 1 2 57.27 3.98 1.6087 3 2 0 4 58.12 4.37 1.5871 1 3 1 4 59.04 5.97 1.5646 1 0 3 2 59.81 3.99 1.5464 0 1 3 2 60.13 1.31 1.5387 2 2 2 4 60.57 12.95 1.5287 4 0 0 2 60.64 2.31 1.5271 3 2 1 4 61.11 24.49 1.5165 2 3 0 4 61.89 1.86 1.4992 1 1 3 4 62.03 2.19 1.4961 3 1 2 4 63.38 1.65 1.4676 4 1 0 4 66.57 2.77 1.4048 4 1 1 4 67.86 1.63 1.3811 1 3 2 4 67.93 19.95 1.3799 2 1 3 4 68.10 9.04 1.3769 0 2 3 2 70.05 2.57 1.3433 1 2 3 4 70.18 1.04 1.3410 3 2 2 4 71.45 3.18 1.3204 4 2 0 4 73.16 6.14 1.2936 4 0 2 2 73.65 11.73 1.2862 2 3 2 4 74.01 2.79 1.2808 1 4 0 4 74.11 5.61 1.2794 3 3 1 4 74.47 2.51 1.2741 4 2 1 4 74.92 3.02 1.2675 3 0 3 2 75.12 1.76 1.2646 0 4 1 2 75.77 3.02 1.2555 2 2 3 4 77.48 1.27 1.2320 3 1 3 4 80.68 3.35 1.1910 5 1 0 4 81.09 3.81 1.1860 5 0 1 2 82.55 4.73 1.1686 2 4 1 4 82.83 4.04 1.1653 1 3 3 4 83.21 2.14 1.1610 1 1 4 4 83.31 1.66 1.1599 4 2 2 4 84.16 1.43 1.1503 4 3 0 4 85.01 2.54 1.1410 3 2 3 4 85.77 1.23 1.1328 1 4 2 4 86.21 1.76 1.1282 2 0 4 2 88.79 4.12 1.1019 3 4 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.