In(PO4)*H2O Tang X J, Lachgar A Inorganic Chemistry 37 (1998) 6181-6185 The missing link: synthesis, crystal structure, and thermogravimetric studies of InPO4*H2O _database_code_amcsd 0012721 CELL PARAMETERS: 5.4342 5.5508 6.5446 97.593 94.558 107.565 SPACE GROUP: P-1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 185.064 Density (g/cm3): 4.087 MAX. ABS. INTENSITY / VOLUME**2: 32.85974003 RIR: 2.618 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.76 9.67 6.4353 0 0 1 2 16.99 1.72 5.2201 0 1 0 2 17.25 55.78 5.1394 1 0 0 2 20.05 100.00 4.4282 -1 1 0 2 20.07 49.83 4.4253 0 -1 1 2 20.71 19.29 4.2886 -1 0 1 2 23.48 4.43 3.7893 1 0 1 2 23.64 27.78 3.7629 0 1 1 2 24.04 6.91 3.7011 1 -1 1 2 27.72 81.21 3.2176 0 0 2 2 27.95 41.24 3.1924 1 1 0 2 28.91 29.19 3.0883 -1 -1 1 2 30.14 8.12 2.9653 0 -1 2 2 33.22 17.52 2.6965 -1 2 0 2 33.49 24.03 2.6756 1 1 1 2 33.66 41.72 2.6630 -2 1 0 2 33.94 8.28 2.6417 1 -1 2 2 34.36 18.55 2.6101 0 2 0 2 34.71 2.59 2.5844 1 0 2 2 34.71 11.14 2.5841 1 -2 1 2 34.91 2.35 2.5702 0 -2 1 2 34.92 1.34 2.5697 2 0 0 2 34.97 22.58 2.5660 -1 1 2 2 35.08 1.89 2.5578 0 1 2 2 35.88 1.80 2.5026 -2 1 1 2 35.91 21.17 2.5010 -1 -1 2 2 35.96 2.41 2.4975 -2 0 1 2 37.47 2.44 2.4001 -1 2 1 2 39.32 4.04 2.2911 0 2 1 2 39.36 6.99 2.2890 2 0 1 2 40.75 4.25 2.2141 -2 2 0 2 40.78 1.68 2.2126 0 -2 2 2 41.40 9.68 2.1808 1 -2 2 2 42.13 8.03 2.1451 0 0 3 2 42.14 3.18 2.1443 -2 0 2 2 42.78 18.36 2.1136 2 -2 1 2 42.87 6.82 2.1097 0 -1 3 2 43.06 7.65 2.1006 -2 1 2 2 43.27 9.57 2.0910 -1 -2 1 2 43.35 2.74 2.0872 1 1 2 2 43.57 13.27 2.0771 1 2 0 2 43.62 15.74 2.0749 -1 0 3 2 43.64 4.19 2.0743 -2 2 1 2 43.92 11.30 2.0617 2 1 0 2 45.21 11.60 2.0057 2 -1 2 2 46.10 2.19 1.9689 -1 2 2 2 46.47 5.49 1.9541 1 -1 3 2 46.59 2.79 1.9492 -1 -1 3 2 48.31 3.46 1.8840 -2 -1 2 2 48.38 4.61 1.8814 0 2 2 2 48.43 2.03 1.8794 1 2 1 2 48.46 4.79 1.8786 0 1 3 2 49.73 5.92 1.8335 -1 3 0 2 49.94 1.08 1.8260 1 -3 1 2 50.55 2.32 1.8055 -3 1 0 2 50.76 5.56 1.7985 -2 2 2 2 51.52 3.04 1.7740 -3 1 1 2 51.63 1.93 1.7703 1 -2 3 2 51.97 2.93 1.7597 -2 0 3 2 52.15 9.47 1.7539 0 -3 1 2 53.46 7.90 1.7141 -2 3 0 2 53.49 9.77 1.7131 3 0 0 2 53.58 2.81 1.7103 -2 1 3 2 53.59 1.50 1.7100 -3 0 1 2 53.77 2.64 1.7049 3 -1 1 2 53.95 8.72 1.6996 -3 2 0 2 54.31 1.44 1.6893 2 -3 1 2 54.32 1.38 1.6888 1 -3 2 2 55.72 7.48 1.6496 -1 -2 3 2 55.74 9.05 1.6491 1 1 3 2 56.33 1.22 1.6334 2 -1 3 2 56.54 1.19 1.6277 -2 -1 3 2 56.63 2.77 1.6253 -2 3 1 2 56.89 7.32 1.6184 -2 -2 1 2 56.91 2.34 1.6181 2 1 2 2 56.97 4.61 1.6164 1 2 2 2 57.05 3.83 1.6142 0 3 1 2 57.07 3.15 1.6139 0 -1 4 2 57.26 5.52 1.6088 0 0 4 2 57.38 5.77 1.6058 3 0 1 2 57.61 3.42 1.6000 -1 2 3 2 57.68 6.25 1.5982 -3 0 2 2 59.04 5.00 1.5647 2 -2 3 2 59.06 3.81 1.5640 2 -3 2 2 59.52 3.27 1.5531 2 0 3 2 59.54 5.97 1.5527 -1 -1 4 2 60.17 6.51 1.5379 0 2 3 2 60.42 2.82 1.5321 -1 -3 1 2 60.70 1.22 1.5257 3 -1 2 2 61.20 8.09 1.5144 -3 2 2 2 61.31 2.76 1.5119 -1 3 2 2 61.48 2.84 1.5083 -3 -1 1 2 61.97 4.27 1.4975 -1 1 4 2 62.24 2.31 1.4916 3 -2 2 2 62.26 1.97 1.4913 1 -3 3 2 62.39 3.76 1.4883 2 2 1 2 62.65 1.74 1.4829 1 0 4 2 62.66 1.35 1.4827 0 -2 4 2 63.02 5.36 1.4751 0 -3 3 2 63.21 1.16 1.4709 0 1 4 2 63.44 2.72 1.4663 -2 3 2 2 64.28 6.98 1.4491 1 -2 4 2 64.32 2.57 1.4484 3 -3 1 2 64.32 1.68 1.4484 -2 0 4 2 64.80 2.55 1.4387 3 0 2 2 64.92 3.03 1.4364 -3 1 3 2 65.28 1.40 1.4292 -3 3 1 2 66.06 2.46 1.4143 1 3 1 2 66.44 1.85 1.4072 3 1 1 2 66.46 5.73 1.4068 -2 -2 3 2 67.80 6.98 1.3822 1 -4 1 2 68.12 1.34 1.3765 2 1 3 2 69.61 1.24 1.3506 -4 1 0 2 69.69 3.69 1.3492 2 -1 4 2 69.77 2.38 1.3479 2 -4 1 2 69.86 1.20 1.3464 -4 1 1 2 70.76 1.56 1.3315 -4 2 0 2 71.00 3.02 1.3276 -3 -1 3 2 72.36 3.83 1.3059 -1 4 1 2 72.84 2.34 1.2984 4 -1 1 2 73.32 3.15 1.2911 -2 3 3 2 73.56 2.37 1.2875 -4 1 2 2 73.57 1.29 1.2874 -1 0 5 2 73.74 1.48 1.2848 4 0 0 2 73.86 1.03 1.2830 -2 2 4 2 74.97 1.65 1.2668 2 3 0 2 75.23 4.17 1.2631 3 0 3 2 75.84 1.36 1.2545 -3 0 4 2 75.85 1.48 1.2543 0 3 3 2 76.12 1.38 1.2505 -2 -2 4 2 77.11 2.08 1.2369 1 -4 3 2 78.28 2.18 1.2213 2 -3 4 2 78.76 1.01 1.2151 -1 -3 4 2 79.13 1.17 1.2103 4 -2 2 2 79.94 1.13 1.2000 -2 4 2 2 80.03 1.34 1.1990 -3 3 3 2 80.29 1.01 1.1957 -1 -2 5 2 80.55 1.03 1.1925 -4 1 3 2 81.32 1.51 1.1832 2 2 3 2 81.65 1.77 1.1792 -3 2 4 2 81.75 1.92 1.1781 -4 -1 1 2 82.50 1.37 1.1693 -4 0 3 2 83.47 1.38 1.1581 3 -1 4 2 83.60 1.39 1.1566 -4 3 2 2 84.94 2.46 1.1418 1 3 3 2 86.32 1.33 1.1270 0 -3 5 2 86.43 1.21 1.1259 1 1 5 2 86.59 1.27 1.1242 1 -4 4 2 86.94 1.16 1.1206 -1 -4 3 2 87.27 2.31 1.1172 4 1 1 2 88.27 1.10 1.1071 -4 4 0 2 88.35 1.18 1.1063 0 -4 4 2 88.52 1.53 1.1046 3 -3 4 2 89.08 1.20 1.0991 4 -1 3 2 89.33 1.05 1.0966 4 -4 1 2 89.44 1.48 1.0956 -4 -1 3 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.