Selenium
      Akahama Y, Kobayashi M, Kawamura H
      Japanese Journal of Applied Physics 31 (1992) 1621-1624
      Structural study on pressure-induced phase transition from beta-Po type to bcc in selenium at 140 GP
      Locality: synthetic
      Sample: at P = 146.5 GPa
      Note: structure known as bcc, phase Se VI
      _database_code_amcsd 0012752

      CELL PARAMETERS:    2.8076   2.8076   2.8076   90.000   90.000   90.000
      SPACE GROUP: Im3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     22.131
      Density (g/cm3):     11.847
      MAX. ABS. INTENSITY / VOLUME**2:      604.4890983    
      RIR:     16.614
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                45.70        100.00        1.9853    1   1   0        12
                66.62         14.88        1.4038    2   0   0         6
                84.53         29.07        1.1462    2   1   1        24
================================================================================