Fe1.15 Ga0.85 O3 Bertaut E, Bassi G, Buisson G, Chappert J, Delapalme A, Pauthenet R, Rebouillat H, Aleonard R Journal de Physique 27 (1966) 433-448 Etude par effet Moessbauer, rayons X, diffraction neutronique et mesures magnetiques de Fe1.15 Ga.85 O3 _cod_database_code 1008838 _database_code_amcsd 0016706 CELL PARAMETERS: 8.7500 9.4000 5.0700 90.000 90.000 90.000 SPACE GROUP: Pc2_1n X-RAY WAVELENGTH: 1.541838 Cell Volume: 417.008 Density (g/cm3): 5.460 MAX. ABS. INTENSITY / VOLUME**2: 47.11989215 RIR: 2.810 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.83 11.21 6.4047 1 1 0 2 18.88 3.11 4.7000 0 2 0 1 20.24 2.81 4.3868 1 0 1 4 20.30 3.41 4.3750 2 0 0 2 22.36 1.39 3.9752 1 1 1 4 26.92 5.90 3.3123 2 0 1 4 27.82 15.62 3.2069 1 2 1 4 27.86 15.99 3.2023 2 2 0 2 28.57 6.53 3.1240 2 1 1 4 30.30 44.88 2.9499 1 3 0 2 32.13 1.56 2.7857 3 1 0 2 33.09 100.00 2.7075 2 2 1 4 35.20 18.69 2.5497 1 3 1 4 35.41 11.89 2.5350 0 0 2 2 35.51 15.56 2.5282 3 0 1 4 36.72 19.65 2.4476 0 1 2 2 36.81 33.75 2.4414 3 1 1 4 36.92 3.60 2.4349 1 0 2 4 38.30 6.56 2.3500 0 4 0 1 39.59 12.90 2.2762 2 3 1 4 40.43 3.05 2.2312 0 2 2 2 40.52 5.50 2.2265 3 2 1 4 41.27 5.86 2.1875 4 0 0 2 41.78 18.03 2.1620 1 2 2 4 45.14 4.14 2.0085 4 0 1 4 45.64 2.04 1.9876 2 2 2 4 45.75 6.29 1.9832 4 2 0 2 46.06 1.76 1.9708 0 3 2 2 46.13 3.19 1.9676 3 3 1 4 47.28 8.44 1.9226 1 3 2 4 47.44 3.88 1.9166 2 4 1 4 47.52 2.42 1.9133 3 0 2 4 48.56 1.04 1.8749 3 1 2 4 49.34 4.51 1.8469 4 2 1 4 49.60 5.28 1.8381 1 5 0 2 50.81 2.65 1.7969 2 3 2 4 52.99 1.95 1.7280 1 5 1 4 53.14 8.52 1.7234 0 4 2 2 53.22 7.54 1.7212 3 4 1 4 53.24 3.00 1.7204 5 1 0 2 54.25 1.93 1.6909 4 3 1 4 54.25 2.74 1.6909 1 4 2 4 55.48 1.28 1.6561 4 0 2 4 58.40 1.40 1.5802 3 5 0 2 58.95 2.26 1.5667 0 6 0 1 59.04 5.21 1.5647 1 2 3 4 59.15 1.22 1.5620 4 2 2 4 59.45 1.64 1.5548 2 1 3 4 60.61 14.97 1.5279 5 3 0 2 60.65 1.76 1.5268 4 4 1 4 61.40 12.46 1.5101 0 5 2 2 61.46 27.08 1.5086 3 5 1 4 62.41 1.14 1.4881 1 5 2 4 63.54 2.50 1.4642 4 3 2 4 63.63 22.43 1.4623 3 0 3 4 63.83 7.23 1.4583 6 0 0 2 65.58 1.67 1.4236 5 1 2 4 65.96 2.33 1.4162 2 6 1 4 66.38 14.97 1.4083 2 3 3 4 66.74 2.31 1.4015 6 0 1 4 68.09 12.03 1.3770 5 2 2 4 70.69 1.17 1.3327 0 6 2 2 70.75 1.79 1.3317 3 6 1 4 71.02 2.40 1.3273 1 7 0 2 72.19 3.83 1.3086 5 3 2 4 73.79 3.02 1.2840 1 7 1 4 75.16 1.79 1.2641 6 0 2 4 75.72 2.28 1.2561 0 1 4 2 75.96 1.50 1.2528 6 1 2 4 76.56 1.98 1.2445 2 7 1 4 76.68 1.54 1.2427 4 5 2 4 76.77 3.25 1.2415 3 4 3 4 76.95 1.05 1.2391 6 4 0 2 77.62 1.21 1.2300 4 3 3 4 79.00 3.59 1.2120 1 2 4 4 79.31 1.00 1.2080 2 5 3 4 79.65 1.22 1.2037 7 1 1 4 81.93 1.23 1.1759 1 7 2 4 84.62 1.12 1.1453 2 7 2 4 87.66 1.17 1.1132 6 4 2 4 88.24 2.65 1.1074 2 8 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.