Al1.06 D5.11 La0.98 Ni3.96 Achard J, Givord F, Percheron-Guegan A, Soubeyroux J Journal de Physique 40 (1979) 218-220 Neutron study of Al or Mn substituted La Ni5 hydrogen sponges _cod_database_code 1009070 _database_code_amcsd 0016931 CELL PARAMETERS: 5.3100 5.3100 4.2490 90.000 90.000 120.000 SPACE GROUP: P6/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 103.754 Density (g/cm3): 6.433 MAX. ABS. INTENSITY / VOLUME**2: 150.1683971 RIR: 7.601 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.91 9.19 4.2490 0 0 1 2 28.60 37.88 3.1208 1 0 1 12 33.76 34.82 2.6550 1 1 0 6 39.18 29.18 2.2993 2 0 0 6 40.05 100.00 2.2516 1 1 1 12 42.55 25.49 2.1245 0 0 2 2 44.82 6.58 2.0222 2 0 1 12 55.39 14.45 1.6588 1 1 2 12 57.27 8.87 1.6087 2 1 1 24 59.21 14.54 1.5604 2 0 2 12 60.39 5.30 1.5329 3 0 0 6 64.64 19.94 1.4419 3 0 1 12 69.44 2.21 1.3536 1 0 3 12 71.00 13.05 1.3275 2 2 0 6 74.95 1.02 1.2671 2 2 1 12 76.18 11.14 1.2496 1 1 3 12 76.66 4.54 1.2431 3 0 2 12 78.26 2.91 1.2216 3 1 1 24 79.48 1.03 1.2059 2 0 3 12 84.22 2.17 1.1496 4 0 0 6 86.44 13.69 1.1258 2 2 2 12 89.20 1.99 1.0980 2 1 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.